Abstract
Thermal annealing has often been used to reduce residual stress and improve mechanical properties and performance of hard coatings. In this work, nanocomposite TiSiN coatings were engineered onto steel substrates by reactive unbalanced magnetron sputtering. Following deposition, thermal annealing was performed at temperatures up to 900 °C. A marked decrease in residual stress was observed in the coatings with the increase of thermal annealing temperature. To ascertain the role of residual stress in the response of the coatings to contact damage, nanoindentation was used to probe the damage resistance of the coatings and Rockwell-C test used to evaluate their adhesion strength, as a function of thermal annealing temperature. A combination of high damage resistance and good adhesion strength was observed for the coating annealed at an intermediate temperature of 600 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.