Abstract
In this work, we investigated structural, electrical, and magnetic properties of ferroelectric PbZr0.2Ti0.8O3 (PZT) and ferrimagnetic/ferroelectric [CoFe2O4(CFO)/PZT] bilayers grown on (100)LaAlO3 (LAO) substrates supplied with bottom 50 nm thick LaNiO3 electrodes. Interestingly, structural and electrical properties of the PZT layer exhibited remarkable changes after the top-layer CFO deposition. X-ray diffraction data suggested that both the c- and a-domains exist in the PZT layer and the tetragonality of the PZT decreases upon the top-layer deposition. A variation in the electrical properties of the PZT layer upon the CFO deposition was investigated by polarization versus voltage (P-V), capacitance versus voltage (C-V), and capacitance versus frequency (C-f) measurements. The CFO deposition induced a slight decrease of the remnant polarization and more symmetric behavior of P-V loops as well as led to the improvement of fatigue behavior. The tentative origin of enhanced fatigue endurance is discussed based on the measurement results. These results were corroborated by local piezoelectric measurements. Ferrimagnetic property of the CFO/PZT bilayer was confirmed by magnetic measurement at room temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.