Abstract
In this paper, the corrosion behaviour of thermal sprayed and diffusion-coated materials are compared. The result of the high temperature corrosion test shows that the layers with NiCr applied by atmospheric plasma spraying (APS) and high velocity oxy fuel flame spraying (HVOF) are more resistant than the layers with NiCrBSi and Cr3C2/ NiCr. Furthermore, the layer with NiCr on 15 Mo 3 is more resistant than that on 13 CrMo 44 as base material. The corrosion behaviour of Al, Cr, and Cr/Si diffusion-coated materials on 13 CrMo 44- are better than those same diffusion coatings on 15 Mo 3-surfaces. In particular, the Cr diffusion-coated materials show the highest corrosion resistances in this work. Also, the diffusion-coated materials have higher resistances than thermal sprayed materials in HCl-H2O-O2-N2-atmosphere. Vergleich des Korrosionsverhaltens von thermisch gespritzten und diffusionsbeschichteten Werkstoffen In der vorliegenden Veroffentlichung wird das Korrosionsverhalten von thermisch gespritzten und diffusionsbeschichteten Werkstoffen verglichen. Das Ergebnis von Hochtemperaturkorrosionsprufungen zeigt, dass die Schicht mit NiCr durch atmospharisches Plasmaspritzen (APS) und Hochgeschwindigkeitsflammspritzen (HVOF) bestandiger ist als die Schichten aus NiCrBSi und Cr3C2/NiCr. Desweiteren ist die Schicht mit NiCr auf 15 Mo 3 bestandiger als solche auf 13 CrMo 44 als Grundwerkstoff. Im Gegensatz dazu ist das Korrosionsverhalten der diffusionsbeschichteten Werkstoffe auf 13 CrMo 44- besser als auf 15 Mo 3-Oberflachen. Besonders die diffusionsbeschichteten Werkstoffe mit Cr zeigen hochste Korrosionsbestandigkeiten. Auserdem haben die diffusionsbeschichteten Werkstoffe hohere Bestandigkeiten als die thermisch gespritzten Werkstoffe gegen HCl-H2O-O2-N2-Atmospharen.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have