Comparative study on biodegradation and biocompatibility of multichannel calcium phosphate based bone substitutes.

Abstract

The objective of this study was to fabricate multichannel biphasic calcium phosphate (BCP) and β-tricalcium phosphate (TCP) bone substitutes and compare their long-term biodegradation and bone regeneration potentials. Multi-channel BCP and TCP scaffolds were fabricated by multi-pass extrusion process. Both scaffolds were cylindrical with a diameter of 1-mm, a length of 1-mm, and seven interconnected channels. Morphology, chemical composition, phase, porosity, compressive strength, ion release behavior, and in-vitro biocompatibility of both scaffolds were studied. In-vivo biodegradation and bone regeneration efficacies of BCP and TCP were also evaluated using a rabbit model for 1week, 1month, and 6months. BCP exhibited superior compressive strength compared to TCP scaffold. TCP showed higher release of both calcium ions and phosphorous ions than BCP in SBF solution. Both scaffolds showed excellent in-vitro biocompatibility and upregulated the expression of osteogenic markers of MC3T3-E1 cells. In-vivo studies revealed that both cylindrical TCP and BCP scaffolds were osteoconductive and supported new bone formation. Micro-CT data showed that the bone-regeneration efficacy of TCP was higher at one month and at six months after implantation. Histological examination confirmed that TCP degraded faster and had better bone regeneration than BCP after 6months.