Abstract
Laser gas assisted nitriding of Ti–6Al–4V alloy is carried out and nitride compounds formed and their concentration in the surface vicinity are examined. SEM, XRD and XPS are accommodated to examine the nitride layer characteristics. Microhardness across the nitride layer is measured. Temperature field and nitrogen distribution due to laser irradiation pulse is predicted. It is found that the nitride layer appears like golden color; however, it becomes dark gold color once the laser power irradiation is increased. The δ-TiN and ɛ-TiN are dominant phases in the surface vicinity. The needle like dendrite structure replace with the feathery like structure in the surface region due to high nitrogen concentration. No porous or microcracks are observed in the nitrided layer, except at high power irradiation, in this case, elongated cracks are observed in the surface region where the nitrogen concentration is considerably high.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.