Abstract
Polycrystalline Gd0.15Ca0.85MnO3 sample was prepared by solid state reaction method and nanocrystalline samples of different grain sizes of the same were prepared by sol–gel method. Phase purity and composition were verified by room temperature X-ray diffraction and SEM-EDAX analysis. Magnetization data of bulk Gd0.15Ca0.85MnO3 in 5kOe field shows a peak at ~119K (TN) suggesting an antiferromagnetic transition. Nanocrystalline Gd0.15Ca0.85MnO3 sample (~54nm size) also shows a cusp at ~107K and a broad thermal hysteresis between field cooled cooling (FCC) and field cooled warming (FCW) data around this temperature. This thermal hysteresis suggests possible crystal structural transition. Field variation of magnetization of bulk Gd0.15Ca0.85MnO3 at 5K shows a tendency to saturate, but yields a magnetic moment value of only ~1.12μB/f.u. in 70kOe. The value of magnetization of nanocrystalline sample at 5K in 70kOe field is slightly larger and is ~1.38μB/f.u. which is probably due to the surface moments of the nanoparticle samples. Both the samples show Curie–Weiss-like behaviour in their paramagnetic state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.