Abstract
Nanocrystalline La0.15Ca0.85MnO3 samples of various grain sizes ranging from ∼17 to 42 nm have been prepared by sol-gel technique. Phase purity and composition were verified by room temperature x-ray diffraction and SEM-EDAX analysis. The bulk La0.15Ca0.85MnO3 is known to order antiferromagnetically around 170 K and to undergo a simultaneous crystal structural transition. DC magnetization measurements on 17 nm size La0.15Ca0.85MnO3 show a peak at ∼130 K (TN) in zero-field-cooled (ZFC) state. Field-cooled magnetization bifurcates from ZFC data around 200 K hinting a weak ferromagnetic component near room temperature due to surface moments of the nanoparticle sample. Low temperature powder neutron diffraction experiments reveal that the incomplete structural transition from room temperature orthorhombic to low temperature orthorhombic-monoclinic state also occurs in the nanoparticle sample as in the bulk. Magnetization in the ordered state decreases as particle size increases, thus indicating the reduction of the competing ferromagnetic surface moments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.