Bipolar Resistive Switching in Hafnium Oxide-Based Nanostructures with and without Nickel Nanoparticles

Abstract

As research into additives and intentionally introduced impurities in dielectric thin film for enhancing the resistive switching based random access memories (RRAM) continues to gain momentum, the aim of the study was to evaluate the effects of chemically presynthesised Ni nanoparticles (NPs) embedded in a dielectric layer to the overall structure and resistive switching properties. HfO2-based thin films embedded with Ni NPs were produced by atomic layer deposition (ALD) from tetrakis(ethylmethylamino)hafnium (TEMAH) and the O2 plasma ALD process onto a TiN/Si substrate. The Ni NPs were separately synthesised through a continuous flow chemistry process and dispersed on the dielectric layer between the two stages of preparing the HfO2 layer. The nanodevices’ morphology and composition were analysed with physical characterisation methods and were found to be uniformly dispersed across the sample, within an amorphous HfO2 layer deposited around them. When comparing the resistive switching properties of otherwise identical samples with and without Ni NPs, the ILRS/IHRS ratio rose from around a 4 to 9 at 0.2 V reading voltage, the switching voltage dropped from ~2 V to ~1.5 V, and a distinct increase in the endurance characteristics could be seen with the addition of the nanoparticles.