Abstract

Silicon carbide fiber-reinforced SiC matrix composites are promising candidates as fuel cladding for several concepts of Generation IV reactors and as structural materials for fusion reactors. The composites used in this study were composed of a SiC matrix obtained by chemical vapor infiltration associated with various fiber types (Tyranno Type-S, Tyranno SA Grade-3 and Hi-Nicalon Type-S) and with a PyC layer as the interphase. 12MeV Au ions were used for irradiation up to 0.05 and 1 displacement per atom (dpa) fluences at room temperature and 800°C. Analysis of both microstructure and composition of composites were performed by scanning electron microscopy (SEM), electron probe microanalysis and Raman spectroscopy. At room temperature and low fluence, Raman spectroscopy results showed that irradiation induces a disordered/distorted state into fibers and matrix. With increasing fluence, a total amorphization of these constituents occurs. The increase in the irradiation temperature leads to a damage recovery and partial recrystallization of samples. Image analysis performed from SEM micrographs highlights no significant change in fiber diameter and shape. However, SEM analysis suggests a longitudinal shrinkage of Tyranno Type-S fibers for the composite irradiated at 1dpa at room temperature and 800°C. These results are in complete agreement with conclusions from neutron irradiations suggesting an appropriate relevance of irradiations with 12MeV Au.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.