Abstract
As the degradation of polymer electrolyte membranes (PEMs) shows catastrophic failures with pinholes and cracks, studies on PEM degradation are essential to improve the reliability and lifetime of polymer electrolyte membrane fuel cell (PEMFC) membrane electrode assemblies (MEAs). However, the investigation of the degradation patterns and understanding of the degradation mechanisms of PEMs are still very limited at the PEMFC MEA level. Herein, open-circuit voltage (OCV) hold (chemical degradation) and humidity cycle test (mechanical degradation) protocols are applied to assess the durability of membrane components of PEMFC MEAs. OCV hold test is conducted at low relative humidity (30%) and OCV condition for 540 h. Humidity cycle test (5000 cycles) is carried out under repeating low (0%) and high (150%) relative humidities. We investigate degradation patterns and mechanisms of PEMs for MEAs after OCV hold and humidity cycle tests using various electrochemical and physicochemical analyses tools. The present study, by providing fundamental understanding of major degradation mechanisms, generates scientific information regarding design tools for the fabrication of highly durable PEMs. Additionally, this study, through accelerated degradation tests, can provide baseline information regarding the durability and lifetime of PEMs by statistically analyzing the deterioration pattern of MEAs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.