Abstract
This research aims at studying aluminum tantalum oxide thin films (AlxTayOz) deposited at low temperature for dielectric applications. These ternary oxide layers are synthesized at 180 °C by physical vapor deposition (PVD), specifically the mid-frequency pulsed direct current reactive magnetron sputtering. The deposition process uses targets made of a mixture of aluminum and tantalum in various proportions. Four target compositions are studied containing 95 at.%, 90 at.%, 80 at.%, and 70 at.% of aluminum, corresponding to 5 at.%, 10 at.%, 20 at.%, and 30 at.% of tantalum, respectively. The ternary oxide thin films of AlxTayOz are compared to aluminum oxide (AlxOz) and tantalum oxide (TayOz) layers produced in the same experimental conditions. The AlxTayOz thin films are dense, uniform, and amorphous regardless of the experimental conditions used in this study. Their chemical composition changes as a function of the target composition. The oxygen flow used during deposition also affects the chemical composition of the oxide layers and the deposition rate. The oxide thin films with tantalum are deposited at higher deposition rates and contain more oxygen. Tantalum also promotes the amorphization of the oxide layers. The highest dielectric strength is measured for the thin film containing a low amount of tantalum combined with a high amount of oxygen.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.