Abstract
(Ba 0.5Sr 0.5)TiO 3 (BST) coating was applied to the etched aluminum foils by sol–gel dip-coating with (Ba 0.5Sr 0.5)TiO 3 sol prepared by mixing tetrabutyl titanate, barium acetate, strontium acetate, diethylene glycol, acetic acid and distilled water. After annealing under 500–600 °C in air, Al 2O 3–BST composite oxide film was formed on the surface of the etched aluminum foil by anodizing galvanostatically in a neutral adipite and borate solution. The BST powders annealed under different temperatures were characterized by TG–DTA and X-ray diffraction (XRD), and the specific capacitance of the coated samples annealed under different temperatures and times was measured. It was experimentally shown that the specific capacitance of the samples with BST coating is greater than without BST coating. The composite films are promising to be used as the dielectric of electrolytic capacitor.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.