Interfaces of two different babbitt-bronze composites were tested ultrasonically and then were fractured using the Chalmers test method. The primary distinction between the two composites was in the copper content. Use of less copper in the babbitt resulted in interfaces with higher strength, lower ductility, less cracking, and less unbonded area. The differences appeared to stem from the structure of the intermetallic compounds found at the interface, namely, the Cu3Sn and the Cu6Sn5 layers. The low-copper composite failed within a thick, dendrite-like Cu6Sn5 layer, while the high-copper one separated at the interface between a smooth Cu6Sn5 layer and the babbitt metal. The rough interface morphology seemed responsible for the low-copper composite’s increased strength. The correlation between mechanical and ultrasonic properties was poor for the low-copper composite but excellent for the high-copper one. These results suggest that interface morphology can significantly affect mechanical as well as ultrasonic properties.