Titanium Source Research Articles

Titanyl sulfate-based TiO2-paraffin phase change microcapsules: Evaluation of alkyltriethoxysilane modification and thermoregulation applications

Titanium dioxide (TiO2) phase change microcapsules show promising applications in building temperature regulation and heat transfer due to their high thermal reflectivity and high thermal conductivity. Currently, the preparation of TiO2 microcapsules predominantly relies on expensive and highly toxic titanate as a raw material. In this study, a new type of TiO2-paraffin phase change microcapsules was prepared by chemical precipitation method using cheap and low toxic titanium sulfate dihydrate (TSD) as titanium source and alkyltriethoxysilane as modifier. The results showed that when methyltriethoxysilane was used as a modifier and the dosage was 1/3 of TSD, the core-wall ratio was 1:1, and the reaction temperature was 65 °C, the performance of the modified TiO2 phase change microcapsules was the best. The melting enthalpy was 112.8 J/g, the core material content reached 83.70 %, which was 48.06 % higher than that of the unmodified microcapsules, and the melting permeability ratio was 12.88 %. The test chamber containing the sample TiO2 phase change microcapsules underwent a temperature rise-cooling test, transitioning from 25 ℃ to 65 ℃ under simulated solar light conditions. The heating time for the phase change microcapsules with modified TiO2 was 28 % faster compared to those containing unmodified TiO2, while the cooling time was 13.00 % slower. It is shown that the light conversion, as well as the thermal storage capacity of TiO2 phase change microcapsules, are significantly improved after organosilicon modification.

A facile synthesis procedure for Engelhard titanosilicate (ETS-4) and its Cs+ and Sr2+ ion exchange properties

This manuscript reports an environmentally benign method for the synthesis of Engelhard titanosilicate (ETS-4) using titanium isopropoxide or anatase as titanium source and citric acid as complexing agent. Slow release of Ti from the hydroxide or oxide precursors through the citric acid complex plays crucial role in formation of titanosilicate. Characterizations of the prepared material were carried out by powder X-ray diffraction (XRD), Scanning Electron Microscope – Energy Dispersive X-ray spectroscopy (SEM-EDS), Thermogravimetric – Differential Thermal Analysis (TG-DTA) and ion exchange studies. Caesium and strontium exchange capacities of the synthesised ETS-4 were found to be 220 mg/g and 76.2 mg/g, respectively. The saturation exchange equilibrium was attained within 60 min.

Preparation of highly hydrophilic cesium ion sieve and its performance in adsorbing Cs+

The unique properties of cesium compounds have garnered increasing attention, among which Cs2Ti6O13 shows great potential for applications. This paper synthesized Cs2Ti6O13(CTO-3) using a template-assisted solvothermal method with cesium carbonate as the cesium source and tetrabutyl titanate as the titanium source. Among them, F127 and hexadecylamine are used as template agents to modulate the surface morphology and hydrophilicity of the precursor. The cesium ion sieve H2Ti6O13 (HTO-3) synthesized after hydrochloric acid pickling has a large specific surface area and good hydrophilicity. This structure is conducive to the ion exchange between Cs+ and H+, resulting in a fast adsorption rate. It is completed within 2 h, and the adsorption capacity reaches 360 mg/g, which is significantly greater than that of the traditional high-temperature solid-phase method. The adsorption process of Cs+ on HTO-3 is more consistent with the pseudo-second-order kinetic equation model, and the adsorption process is chemical adsorption. HTO-3 exhibited good selectivity and cycle stability. At the fifth time of the adsorption-resolution cycle, the adsorption capacity was 87.1 % of the first time.

The Utilization of Rice Husk as Both the Silicon Source and Mesoporous Template for the Green Preparation of Mesoporous TiO2/SiO2 and Its Excellent Catalytic Performance in Oxidative Desulfurization.

In recent years, TiO2-based catalysts have received extensive attention from researchers for their excellent oxidative desulfurization (ODS) performances. In this paper, a series of mesoporous TiO2/SiO2 catalysts with different TiO2 loadings are prepared, using an incipient wetness impregnation method with agricultural waste rice husk as both the silicon source and mesoporous template and tetrabutyl titanate as the titanium source. The effect of different TiO2 loadings on the ODS performance of the samples is investigated, and the appropriate TiO2 loading is 2.5%. Compared with pure TiO2, the 2.5%TiO2/SiO2 sample exhibits high catalytic activity for oxidative desulfurization. This is, on the one hand, due to the high specific surface area and mesopore volume of the 2.5%TiO2/SiO2 sample. On the other hand, it is due to the uniform dispersion of TiO2 grains with an average diameter of 6.1 nm on the surface of the mesoporous SiO2 carrier, which greatly increases the active sites of the 2.5%TiO2/SiO2 sample, thus improving the catalytic activity of the sample. The recycling performances of the 2.5%TiO2/SiO2 sample are further investigated. The results show that, after fifteen cycles, the 2.5%TiO2/SiO2 sample still maintains high conversions of dibenzothiophene (99.8%) and 4,6-dimethyldibenzothiophene (99.7%) without deactivation. In addition, the 2.5%TiO2/SiO2 sample treated with TBHP aqueous solution is characterized by the technique of UV-Vis, and the Ti-peroxo (Ti-OOtBu) species, the active intermediate for the ODS of bulky organic sulfides, is successfully captured. Finally, a possible reaction mechanism for the ODS process over the 2.5%TiO2/SiO2 sample is proposed.

Construction of NiTiO3/g-C3N4 heterojunction with preferable photocatalytic performance for tetracycline degradation

Tetracycline antibiotics as one of the most widely used antibiotics at present, are difficult to degrade in the environment, which poses a serious threat to the ecosystem and human health. In this work, NiTiO3/g-C3N4 composites were successfully constructed by calcination method using nickel acetate tetrahydrate as nickel source and tetrabutyl titanate as titanium source. The photocatalytic degradation efficiency of the 5 wt% NiTiO3/g-C3N4 composite of TC can reach 88.2 % within 150 min, which was 1.4 and 2.2 times higher than that of pure g-C3N4 (63 %) and NiTiO3 (40 %), respectively. The 5 wt% NiTiO3/g-C3N4 composite can still maintain good stability after four cycles. The experimental results showed that the construction of Z-scheme heterojunction can effectively improve the photocatalytic activity of the catalysts and maintain good redox properties at the same time. Furthermore, a possible mechanism of photocatalytic degradation of NiTiO3/g-C3N4 heterojunction has been suggested.

Silver nanoparticles-promoted bismuth titanate perovskite nanosheets photocatalyst for water purification

Photocatalysis is a recognized approach in the detoxification of pollutants and in water splitting. Such process is more appealing when it is driven by visible or solar light. In this context, we synthesized bismuth titanate perovskite oxide (Bi4Ti3O12, BTO) photocatalyst by sol–gel hydrothermal process. The resulting BTO materials was affected by the titania source and by the synthesis medium pH parameter. Titanium butoxide [Ti(n-BuO)4] was much better than titanium isopropoxide [Ti(i-PrO)4] in producing regular nanosheets with higher surface area, while 75 ml of 5.0 M sodium hydroxide was the optimum concentration for the synthesis of regular, thin, porous, almost equal size nanosheets. The photocatalytic activity of BTO was improved by loading silver nanoparticles (AgNPs) by photo-assisted reduction. The optimum weight percent of loading AgNPs was found to be 1.5 % because it led to the highest light absorbance, the smallest band gap energy, the minimum rate of electron-hole recombination. The photocatalytic degradation efficiency of 1.5 wt% Ag/BTO reached as high as 99.0 % of rhodamine B (RhB, 100 ml, 6 ppm of initial concentration) under 70 min of irradiating visible light (>420 nm). Moreover, pH had a strong influence on the photocatalytic activity of 1.5 wt% Ag/BTO, with pH = 3.0 was the optimum, owing to its impact on the interaction between the positively-charged photocatalyst surface and the negatively-charged RhB molecules. It was found that superoxide radicals played key role in the photocatalytic activity.

Hierarchical two‐dimensional Ti‐MOF derived from MXene for hybrid supercapacitor electrodes

Presently, two‐dimensional (2D) metal–organic framework (MOF) are drawing increasing attention in energy‐storage areas. However, more and complexed factors would affect the nucleation and growth of 2D MOFs, and subsequently affect the final performance. Particularly, it is important to control the coordination rate between ions and ligands. In this paper, MXene was directly used as titanium source to coordinate with an organic ligand to form Ti‐MOF sheets. To further boost the performance, mesopores were introduced in preparing 2D Ti‐MOF, constructing hierarchical porous Ti‐MOF@Ti3C2TX hybrids. Results showed that diffusion‐controlled behaviors play a dominant role over surface capacitive behaviors during the charge storage process of the hierarchical porous hybrids. A hybrid supercapacitor (HSC) assembled with the obtained HP‐Ti‐MOF@Ti3C2TX and activated carbon (AC) exhibited an energy density of 22.9 Wh kg−1 at a power density of 850 W kg−1 (1 A g−1), and a power density of 4.25 kW kg−1 at an energy density of 15.3 Wh kg−1 (5 A g−1). The present strategy is expected to provide design ideas for novel energy‐storage electrode materials.

Photodegradation of dye wastewater by Ti doped Bi2O3/montmorillonite composites

Ti-doped Bi2O3/montmorillonite composites (TBM) were synthesized via chemical solution decomposition using tetrabutyl titanate and bismuth nitrate pentahydrate as titanium and bismuth sources, with sodium montmorillonite as the carrier. The active brilliant blue KN-R, carmine, and rose red B solutions were employed for adsorption and degradation experiments. Characterization of the composite was done through XRD, SEM, BET, and UV-Vis DRS analyses. Results indicate that the optimal degradation performance is achieved when the Ti doping ratio is 4 % (4TBM). The removal rates for active brilliant blue KN-R, carmine, and rose red B solutions were 98.17 %, 98.29 %, and 96.77 %, respectively. Bi2O3 was found in a tetragonal phase, with Ti ions doping into the lattice of Bi2O3 as Ti4+ inhibiting grain growth. The montmorillonite flakes in the composite were exfoliated, leading to an increased specific surface area of 4.16 m2/g. Following Ti doping, Ti 3d, O 2p, and Bi 6 s orbitals combined to form a valence band of 4TBM, reducing the band gap from 2.59 eV to 2.52 eV. This enhancement in light absorption capacity improved the photocatalytic degradation performance of 4TBM.

Low-temperature synthesis, characterization of γ-Li2TiO3 and applications for lithium ion extraction

In this study, the precursor γ-Li2TiO3 was synthesized utilising the Kirkendall effect, which entailed mixing titanium and lithium sources at the nano-scale and calcining the resulting mixture at a low temperature (923 K). The X-ray diffraction data demonstrated that the crystal cell parameter values of the axial lengths a = b = c are each 8.372 Å and that the axis angles α = β = γ are each 90°, which align with γ-Li2TiO3 parameters. In addition, the characteristic lattice stripes of γ-Li2TiO3 appeared clearly in its transmission electron microscopy images. The chemical compound γ-H2TiO3 was derived from the precursor γ-Li2TiO3 through pickling. Because of the cavity effect of the lithium-ion sieve used, only H+ and Li+ could enter and exit the sieve freely, resulting in the selective adsorption of Li+. The Li+ adsorption capacity of γ-H2TiO3 was high (74.85 mg g−1) with good selectivity. The adsorption behaviour of Li+ followed the Langmuir monolayer molecular adsorption behaviour and could be determined using the chemisorption kinetic model. Moreover, γ-H2TiO3 exhibited superior adsorption capacity than layered titanium-ion sieves and the cyclic adsorption of γ-H2TiO3 was more efficient than that of layered titanium-ion sieves. Thus γ-H2TiO3 can be used in industrial applications involving lithium extraction.

Low-Grade Ilmenite Leaching Kinetics Using Hydrochloric Acid: RSM and SCM Approaches

Minerals containing TiO2 are common in Indonesia, such as ilmenite in iron sand deposits scattered along the country's coasts. Ilmenite is an important source of titanium. One method for making TiO2 from ilmenite is by solubilizing both the Fe and Ti elements in HCl and then immediately hydrolyze the Ti. The leaching of low-grade ilmenite (ground to 0.177-0.149 mm) is studied kinetically by HCl in a stirred reactor. The research was conducted using the caustic fusion method followed by HCl leaching. The leaching reaction kinetics at the optimum conditions are analyzed using response surface methodology (RSM) with a second-order polynomial equation model and SSE with the shrinking core model (SCM). The results showed that HCl concentration and leaching time were directly proportional to the leached titanium concentration. In contrast, the leaching temperature was inversely proportional. The optimum operating conditions were obtained at a temperature of 30 °C, 9 M HCl, and 120 min of leaching time. The shrinking core model is a better representation of the kinetics than RSM with a second-order polynomial equation model. Based on SCM, the rate of the leaching reaction of titanium from low-grade ilmenite is controlled by diffusion through the ash layer.

Preparation and photoelectric properties of photoanode based on N-TiO2 deposited on copper electrode

Reducing the photoresistance of a photoanode is one of the key points to improving the electron transfer rate of dye-sensitive solar cells. With TiO2 sol acting as the titanium source and urea serving as the nitrogen source, the N-doped TiO2 composite electrode material was prepared by electrodeposition on the surface of copper foil. The results show that the N-TiO2/Cu electrode prepared by electrodeposition doping at a voltage of 1.0 V has a low photoresistance and bias of 0.25 V difference with the Cu electrode under visible light. The photocurrent is increased by 270 % in comparison with that of the TiO2/Cu electrode. The N-TiO2/Cu electrode shows good photoresponsivity and has a good potential application in dye-sensitive solar cells.

Waste Biomass-Mediated Synthesis of TiO2/P, K-Containing Grapefruit Peel Biochar Composites with Enhanced Photocatalytic Activity.

In this study, TiO2/P, K-containing grapefruit peel biochar (TiO2/P, K-PC) composites were synthesized in situ biomimetically using grapefruit peel as the bio-template and carbon source and tetrabutyl titanate as the titanium source. This was achieved using the two-step rotary impregnation-calcination method. Adjusting the calcination temperature of the sample in an air atmosphere could regulate the mass ratio of TiO2 to carbon. The prepared samples were subjected to an analysis of their compositions, structures, morphologies, and properties. It demonstrated that the prepared samples were complexes of anatase TiO2 and P, K-containing carbon, with the presence of graphitic carbon. They possessed a unique morphological structure with abundant pores and a large surface area. The grapefruit peel powder played a crucial role in the induction and assembly of TiO2/P, K-PC composites. The sample PCT-400-550 had the best photocatalytic activity, with the degradation rate of RhB, MO, and MB dye solutions reaching more than 99% within 30 min, with satisfactory cyclic stability. The outstanding photocatalytic activity can be credited to its unique morphology and the efficient collaboration between TiO2 and P, K-containing biochar.

Nanostructured Niobium and Titanium Carbonitrides as Electrocatalyst Supports.

Nanostructured niobium-titanium carbonitrides, (Nb,Ti)C1-xNx, with the cubic-rock salt structure are prepared without the use of reactive gases via thermal treatment (700-1200 °C) under nitrogen of mixtures of guanidine carbonate and ammonium niobate (V) oxalate hydrate, with addition of ammonium titanyl oxalate monohydrate as a titanium source. The bulk structure and chemical composition of the materials are characterized using powder X-ray diffraction (XRD) and powder neutron diffraction, elemental homogeneity is studied using energy dispersive spectroscopy (EDS) mapping using transmission electron microscopy (TEM), and surface chemical analysis is examined using X-ray photoelectron spectroscopy (XPS). Nanoscale crystallites of between 10 and 50 nm are observed by TEM, where EDS reveals the homogeneity of metal distribution for the mixed-metal materials. Titanium carbonitrides are found to be air sensitive, reacting with air under ambient conditions, while titanium-niobium carbonitrides are found to degrade in aqueous sulfuric acid. The niobium carbonitrides, however, show some stability toward acidic solutions. Materials are produced with composition NbC1-xNx with x between 0.35 and 0.45, and more carbon-rich materials (x ≈ 0.35) are found as the synthesis temperature is increased, as proven by Rietveld refinement of crystal structure against powder neutron diffraction data. Despite phase purity seen by diffraction and negligible bulk carbon content, XPS shows a complex surface chemistry for the NbC1-xNx materials, with evidence for Nb2O5-like oxide species in a carbon-rich environment. The NbC1-xNx prepared at 900 °C has a surface area around 50 m2 g-1, making it suitable as a catalyst support. Loading with iridium provides a material active for the oxygen evolution reaction in 0.1 M sulfuric acid, with minimal leaching of either Nb or Ir after 1000 cycles.

Selective recovery of La3+ from rare earth mine tailwater by titanium phosphate adsorbents with different crystal forms

Titanium phosphate (TiP) materials in different crystalline forms—amorphous TiP (am-TiP), scaly TiP (s-TiP), platy TiP (p-TiP) and alpha-type TiP (α-TiP) were synthesized by using titanium source of TiOSO4 and phosphorus source of H3PO4. The structures and properties of the four TiP materials and their adsorption selectivity for rare earth La3+ ions were studied. The results showed that the ion exchangeability of TiP was related to the phosphate groups in the structures. The -HPO4 groups dominated the phosphate groups of am- and p-TiP, while -H2PO4 and-HPO4 groups were the only phosphate groups of s- and α-TiP, respectively. La3+ ions were mainly adsorbed through ion exchange with H+ of P-OH groups of TiP. However, the adsorption was not only related to the cation exchange capacity, but also to the structure features of the materials. The adsorption capacity for La3+ was negatively correlated with the crystallinity of TiP, which decreased in the order of 102.25 (am-TiP) >56.08 (s-TiP) > 22.77 (p-TiP) > 6.79 mg⋅g−1 (α-TiP). The adsorption of La3+ by TiP was basically unaffected by the mono- and di-valent impurity ions except for the tri-valent ions, such as Al3+. Additionally, the semi-crystalline s-TiP had the best desorption and regeneration performance among the four TiP.

Boosting the piezo-photocatalytic performance of Na0.5Bi0.5TiO3 by modulating the oxygen vacancy concentration

The emergence of piezo-photocatalysis inaugurates a nascent approach aimed at mitigating the rapid recombination of electrons and holes, thus augmenting catalytic efficacy. This work endeavors to fabricate Na0.5Bi0.5TiO3 (BNT) nanosphere powders through a simplified hydrothermal method, whereby precise control over the quantity of tetrabutyl titanate, a titanium source, is employed. The piezo-photocatalytic performance of BNT nanospheres is meticulously scrutinized through the degradation of Rhodamine B (RhB) at a concentration of 5 mg/L, utilizing ultrasonic vibration and UV–visible light irradiation. Remarkably, the appropriate oxygen vacancies exerts a profound impact on the efficiency of piezoelectric photocatalytic degradation. Among the investigated catalysts, The material with the best performance exhibits the highest rate of piezo-photocatalytic degradation, boasting a rate constant (k value) of 0.052 min−1. Furthermore, the BNT nanospheres exhibit commendable stability and reusability in the context of piezo-photocatalytic degradation. Elucidation of the piezo-photocatalytic mechanism of BNT nanospheres is attained through the identification of radicals and intermediates present in the degradation process. This research imparts invaluable guidance for the design and development of state-of-the-art and high-performance piezo-photocatalytic catalysts.

Non-hydrolytic sol-gel synthesis of BaTiO3 nano-powder: Effect of calcination temperature and modified titanium source on particles

In this study, BaTiO3 nanopowders were prepared by non-hydrolytic sol-gel (NHSG) method using barium acetate and tetrabutyl titanate (TBT) as precursors and acetylacetone (Hacac) as additive. The effects of acetylacetone modification and calcination temperature on nanoparticle size and crystalline phase were evaluated. The products were analysed by SEM, TEM, DSC/TG, FTIR, XRD, Raman. FTIR analysis showed the formation of Ba-O-Ti bond at the sol stage of the NHSG method. DSC/TG and XRD analyses showed that BaTiO3 was produced at 500 ℃. According to SEM/TEM, the particle size of the powder becomes larger as the temperature increases, meanwhile the addition of acetylacetone can make the final product particle size decrease. Raman analysis showed that BaTiO3 has the presence of tetragonal phase, so the crystalline phases of the product and impurities were analysed by XRD refinement, and the results showed that the relative content of tetragonal phase of BaTiO3 was linearly correlated with the calcination temperature.

A H2O2 Oxidation Approach to Ti3C2/TiO2 for Efficient Photocatalytic Removal of Distinct Organic Pollutants in Water.

To develop versatile photocatalysts for efficient degradation of distinct organic pollutants in water is a continuous pursuit in environment remediation. Herein, we directly oxidize Ti3C2 MXene with hydrogen peroxide to produce C-doped anatase TiO2 nanowires with aggregates maintaining a layered architecture of the MXene. The Ti3C2 MXene provides a titanium source for TiO2, a carbon source for in situ C-doping, and templates for nanowire aggregates. Under UV light illumination, the optimized Ti3C2/TiO2 exhibits a reaction rate constant 1.5 times that of the benchmark P25 TiO2 nanoparticles, toward photocatalytic degradations of trace phenol in water. The mechanism study suggests that photogenerated holes play key roles on the phenol degradation, either directly oxidizing phenol molecules or in an indirect way through oxidizing first the surface hydroxyl groups. The unreacted Ti3C2 MXene, although with trace amounts, is supposed to facilitate electron transfer, which inhibits charge recombination. The unique nanostructure of layered aggregates of nanowires, abundant surface oxygen vacancies arising from the carbon doping, and probably the Ti3C2/TiO2 heterojunction guarantee the high photocatalytic efficiency toward removals of organic pollutants in water. The photocatalyst also exhibits an activity superior to, or at least comparable to, the benchmark P25 TiO2 toward photodegradations for typical persistent organic pollutants of phenol, dye molecule of rhodamine B, antibiotic of tetracycline, pharmaceutical wastewater of ofloxacin, and pesticide of N,N-dimethylformamide, when evaluated in total organic carbon removal.

Study on efficient degradation of tetracycline by titania nanoribbons modified with silver

TiO2 nanoribbons were prepared by hydrothermal method using P25 as titanium source, and Ag/TiO2 composites were prepared by REDOX method. Xenon lamp was used as the light source to study the photocatalytic degradation efficiency of tetracycline by Ag/TiO2 and tetracycline degradation efficiency under different conditions. When the initial concentration of tetracycline was 50mg/L, the pH value was 8, and the catalyst dosage was 0.05g. The optimal reaction conditions showed that the degradation efficiency of tetracycline by Ag/TiO2 composite could reach 88.9%, which was 12% higher than that of TiO2.

Comparison of H2O2 and H2O oxidations on TDMAT absorbed on silicon(100) surface during reaction step of ALD–TiO2 process: A DFT study

Atomic layer deposition (ALD) is a thin film technology with high potential in nano fabrication. There is industrial demand to produce an ALD–TiO2 thin film using a low temperature process for applications of bending electronic devices and biomaterials. TDMAT has gained the most attention as a suitable titanium source to grow an ALD–TiO2 film at extremely low temperatures. In this process, almost all published reports have focused on metal-oxide precursors. The current work investigates the effects of oxidizing agents. For the first time, a theoretical investigation was carried out on the oxidation of H2O2 and H2O on TDMAT absorbed on a silicon (100) surface during the reaction step of the ALD–TiO2 process. We simulated the oxidation process, which continued from the adsorption step of the ALD–TiO2 process, where the TDMAT was used as a titanium precursor. The cluster of the Si9H12 =O2 =Ti[N(CH3)]2 surface model was used to represent the remaining TDMAT molecule absorbed on the Si(100) substrate. The reaction mechanisms of H2O2 oxidizing on this surface were evaluated based on their reaction pathways. The reaction pathway of H2O oxidizing on this surface was calculated at the same level to compare the effect of oxidizers. The DFT at the B3LYP 6–311 G+ (2d,p) and 6–31 G(d,p) theoretical levels were used to calculate the potential energy surface and to optimize the electronic structures in this process. It was found that the reaction mechanism depended on the nature of chemical bond dissociation within the oxidizer molecules during the oxidation process. In the oxidation of H2O2, the H2O2 molecule contained O–O and O–H bonds, which were dissociated during the oxidation process, resulting in different product structures. Only the O–O bond dissociation pathway produced the TiO2 structure. The two species of TDMAT ligands at the surface were completely oxidized using a single H2O2 molecule. The H2O2 oxidation produced more –OH groups (double) compared to H2O oxidation. In H2O oxidation, the H2O molecule contained only the O–H bond within its molecule and required activation energies significantly less than for all pathways of H2O2. The HOMO–LUMO properties and IR frequency characteristics (cm−1) of the plausible product structures were discussed. The results should be useful in guiding the selection of suitable precursors for use in the co–reactant system of the ALD–TiO2 process.

Facile Route to Synthesize a Highly Sinterable Li1.3Al0.3Ti1.7(PO4)3 Solid Electrolyte.

NASICON-type Li1.3Al0.3Ti1.7(PO4)3 (LATP) is a widely used solid electrolyte in solid-state lithium batteries, owing to its excellent chemical stability against moisture and high total ionic conductivity. However, traditionally, densification of LATP has been achieved through a high-temperature sintering process (approximately 1000 °C) owing to its poor sinterability. Herein, we report a facile synthesis route to obtain highly sinterable LATP solid electrolyte using tetrabutyl titanate (C16H36O4Ti) as the titanium source and incorporating the traditional solid-state reaction method. The synthetic LATP powder mixed with a low ratio of LiTiPO5 exhibited a hybrid crystalline-amorphous phase structure, which facilitated grain fusion, promoted structural homogeneity, and facilitated structural densification under low-temperature sintering. The sintered LATP pellet, which exhibited an interconnected structure and indistinct grain boundaries, achieved a relative density of >90% and an ionic conductivity of 0.667 mS/cm at a sintering temperature of only 750 °C. Additionally, we systematically studied and demonstrated the synthesis reaction mechanism, sintering behavior, and ionic diffusion kinetics of LATP electrolytes. Our study paves the way for synthesizing highly sinterable LATP solid electrolytes using a simple, additive-free, and cost-effective method.