Ti Content Research Articles

Structural and magnetic properties of rapidly solidified and Bi-bonded hot compacted Mn[formula omitted]Al45C1.7Ti[formula omitted] magnets

This study examines the impact of Ti doping on the phase formation and magnetic properties of Mn-Al-C alloys. Using melt spinning, we synthesized Mn53.3−xAl45C1.7Tix alloys (x values ranging from 0 to 1.5) producing high purity ϵ-phase ribbons. The optimal annealing treatment for the formation of ferromagnetic τ-phase is 20 min at 550 °C for all compositions. However, Ti-doped samples showed the formation of β-phase due to partial phase decomposition, and TiC precipitates were present at high Ti concentrations. Upon doping, the Curie temperature was increased from 557K (Ti free sample) to 600K. To improve the coercivity, a combination of ball milling and hot compaction, introducing Bi as a metallic binder, have resulted in increased coercivity from 0.18 T to 0.33 T. Bi addition lead to formation of a grain boundary phase aiding densification. We demonstrate how modifying composition and processing can improve the magnetic properties of Mn-Al based magnets.

Influence of Al and Ti Alloying and Annealing on the Microstructure and Compressive Properties of Cr-Fe-Ni Multi-Principal Element Alloy

This study meticulously examines the influence of aluminum (Al) and titanium (Ti) on the genesis of self-generated ordered phases in high-entropy alloys (HEAs), a class of materials that has garnered considerable attention due to their exceptional multifunctionality and versatile compositional palette. By meticulously tuning the concentrations of Al and Ti, this research delves into the modulation of the in situ self-generated ordered phases’ quantity and distribution within the alloy matrix. The annealing heat treatment outcomes revealed that the strategic incorporation of Al and Ti elements facilitates a phase transformation in the Cr-Fe-Ni medium-entropy alloy, transitioning from a BCC (body-centered cubic) phase to a BCC + FCC (face-centered cubic) phase. Concurrently, this manipulation precipitates the emergence of novel phases, including B2, L21, and σ. This orchestrated phase evolution enacts a synergistic enhancement in mechanical properties through second-phase strengthening and solid solution strengthening, culminating in a marked improvement in the compressive properties of the HEA.

Genesis of high-grade lode gold shoot dominated by ore fluid overprinting during a ductile-brittle shear event

Lode gold deposits hosted by ductile-brittle shear zones account for more than one-third of the world’s gold production. High-grade ore shoots from this type of deposit are the most critical exploration targets. The ore shoots can form through the post-depositional deformation of auriferous sulfides or overprinting of ore fluids accompanied by coupled dissolution-reprecipitation (CDR) reactions. However, the mechanism that dominates ore shoot genesis remains unknown, primarily due to the controversial single progressive or polyphase nature of ore-bearing shear zones. Here, we report on geological and geochemical analyses we conducted at the large Hetai goldfield, South China, to construct an accurate gold upgrading model for the formation of ore shoots. Stages 1−3 of mineralization at Hetai show features typical of ductile shearing, while Stage 4 is characterized by quartz-sulfide veinlets in brittle fractures. 40Ar/39Ar ages of ca. 184 Ma and 157 Ma for the mineralization of stages 1 and 4 overlap with the regionally dextral ductile-brittle shear that occurred during ca. 210−162 Ma. Thus, the gold event at Hetai should have been controlled by a single progressive ductile-brittle shear episode, rather than polyphase structural events. The auriferous fluids at Hetai precipitated minor invisible gold in pyrites (mean 0.173 ppm) produced during stages 1−4 through fluid-rock interaction. The systematic increase of elements Au, As, Sb, Bi, Ag, and Cu and δ34S values in ductile-deformed pyrites from stages 1−3 indicate that early invisible gold upgrading should be the result of the post-depositional remobilization of auriferous sulfides during the long-lived ductile-brittle transition. Cataclastic pyrites hosting invisible gold from Stage 4 have zoned and porous mantles with elevated invisible gold (mean 0.503 ppm) and Sb, Bi, Pb, Co, Ni, and Ti contents. These pyrites are further replaced by chalcopyrite and pyrrhotite with increasing invisible gold, Co, and Ni contents. In addition, numerous visible native gold grains in Stage 4 are included in sulfides formed by replacement and develop along the microfractures and grain boundaries of these sulfides. We suggest the late invisible and visible gold upgrading events in Stage 4 can be attributed to the auriferous fluid superposition and subsequent replacement of pyrite via CDR reactions in a brittle regime. Therefore, the gold upgrading process at Hetai is jointly caused by the early remobilization induced by ductile-brittle deformation and the late ore fluid superposition with accompanying CDR reactions within a brittle domain. As the ore fluid superposition and CDR reactions in Stage 4 produce a significant amount of visible gold, they exert a first-order control on the genesis of ore shoots at Hetai. The refined model may be widely applicable to lode gold deposits elsewhere and can be used to identify regions with promising exploration targets.

Microstructure and properties behavior of in situ synthesized with high content (Ti, W) C reinforced In625 by two step-laser direct energy deposition

The formation of sensitive interface cracks and the difficulty in processing high-concentration Ni-based ceramic coatings via direct energy deposition (LDED) present major engineering challenges. To address these, high-quality In625/ceramic coatings with various mass contents of Ti, nickel-coated graphite (Ni3C), and WC were fabricated on QT250 using two-step laser directed energy deposition (TsLDED). The influence of the Ti/C: WC molar mass ratio on the bonding interface, microstructure, phase composition, and mechanical properties of the coatings was analyzed. The results indicated that grains at the In625/ceramic coating interface formed epitaxial growth, ensuring a robust bond. In situ synthesis of (Ti, W) C, WCx (WC and W2C), M23C6, and other precipitated phases were uniformly distributed, enhancing nucleation, refining microstructure, and improving mechanical properties. The addition of Ti facilitated the transformation of WCx to (Ti, W) C. High Ti and C concentrations promoted eutectic structure formation in the matrix phase, enhancing performance. The In625 + 56 % Ti – 14 % Ni3C – 30 % WC composite coating exhibited the highest microhardness and the lowest friction coefficient, with microhardness 5.61 and 3.6 times that of QT250 and In625 coatings, respectively, and a friction coefficient 0.3 times that of In625. Variations in the Ti/C: WC molar mass ratio directly affected the content, proportion, and type of (Ti, W) C, WCx, γ-Ni, and eutectic structures comprising M23C6, NiTix, Ni2W4C, Cr2Ti, and γ-Ni, influencing microstructure evolution and mechanical properties. The TsLDED process thus enables the preparation of In625/ceramic reinforced coatings with improved mechanical properties.

Theoretical Insights into Off-Stoichiometric Zr(x)Ti(1-x)IrSb Half-Heusler Alloys: A First Principle Calculations.

This study presents a theoretical investigation into the phase stability, electronic, and optical properties of off-stoichiometric Zr_{x}Ti_{1-x}IrSb (x = 0, 0.0625, 0.1875, 0.25, 0.50, 0.75, 1) compounds. Using first-principles calculations, we explore how varying Zr and Ti concentrations can tune the electronic and optical properties of these half-Heusler alloys. The Structural, optical, and electronic properties were meticulously analyzed with both the GGA-PBE and Meta-GGA-SCAN approximations, as implemented in the Vienna Ab initio Simulation Package (VASP). The dynamical stability of these compounds was assessed using the Phonopy package. Our findings reveal that these alloys exhibit semiconductor behavior with tunable band gaps, and their optical properties show significant variation across different compositions, particularly in the visible light range. The compounds also demonstrate robust dynamical stability, indicating their potential for practical applications in electronic and optoelectronic devices. These results underscore the versatility of Zr_{x}Ti_{1-x}IrSb alloys and highlight their promise for next-generation technology.

Preparation and oxidative desulfurization performances of modified SBA-15 supported polyacid metal oxolates

In this study, eight composite catalysts were prepared by loading (CTAB)3H3[PW9V3O40] (active components) onto amino-functionalized mesoporous titanium silicate Ti-SBA-15(supports). In order to study the effects of different Ti contents and different active components on the catalytic performances of the catalysts, 30 %(CTAB)3H3[PW9V3O40]/NH2–Ti-SBA-X (X = 0, 25, 50, 75, 100) and X%(CTAB)3H3[PW9V3O40]/NH2–Ti-SBA-50 (X = 20, 40, 50) were obtained and characterized. The oxidative desulfurization performances of the composite catalysts were explored. It was found that catalyst 40 %(CTAB)3H3[PW9V3O40]/NH2–Ti-SBA-50 exhibits the optimal oxidative desulfurization performance. This is because the incorporation of SBA-15 with an appropriate amount of Ti (n(Si)/n(Ti) = 50) can improve the acidity and stability of mesoporous silica. The successful substitution of CTAB (n(CTAB)/n(H6PW9V3O40) = 3) in the active component can reduce the mass transfer resistance and speed up the reaction rate. 3-Aminopropyltriethyl silane (APTES) acts as a silane coupling agent to graft amino groups onto mesoporous molecular sieve SBA-15, which can enhance the interaction between heteropolyacids and carriers. Under the synergistic effect of the active component and the support, the total removal rate of the optimal catalyst with a total concentration of 1000 ppm sulfur compounds in the simulated fuel was 94.44 %. After four cycles, the total desulfurization rate of the catalyst can reach 91.28 %.

Analyzing the Influence of Titanium Content in 5087 Aluminum Filler Wires on Metal Inert Gas Welding Joints of AA5083 Alloy

As the demand for lightweight structures in the transportation industry continues to rise, AA5083 aluminum alloy has become increasingly prominent due to its superior corrosion resistance and weldability. To facilitate the production of high-quality, intricate AA5083 components, 5087 aluminum filler wire is commonly utilized in metal inert gas (MIG) welding processes for industrial applications. The optimization of filler wire composition is critical to enhancing the mechanical properties of AA5083 MIG-welded joints. This study investigates the effects of modifying 5087 aluminum filler wires with different titanium (Ti) contents on the microstructure and weldability of AA5083 alloy plates using MIG welding. The influence of Ti contents was systematically analyzed through comprehensive characterization techniques. The findings reveal that the constitutional supercooling induced by the Ti element and the formation of Al3Ti facilitate the heterogeneous nucleation of α(Al), thereby promoting grain refinement. When the Ti content of 5087 filler wire is 0.1 wt.%, the grain size of the weld center was 78.48 μm. This microstructural enhancement results in the improved ductility of the AA5083 MIG-welded joints, with a maximum elongation of 16.64% achieved at 0.1 wt.% Ti addition. The hardness of the joints was the lowest in the weld center zone. This study provides critical insights into the role of Ti content in MIG welding and contributes to the advancement of high-performance filler wire formulations.

Relations of magnetic and electrochemical anti-corrosion properties of (Zr, Ti)-doped NdCeFeB magnets with Ti content

Zr and Ti were co-doped into NdCeFeB sintered magnets to improve the magnetic and electrochemical anti-corrosion properties. Both performance are found closely associated with Ti content. At 0.15 wt%Ti, the sample shows higher coercivity without energy product loss compared to the Ti-free sample and other Ti additions, due to the matrix-phases refinement and optimized distribution of RE-rich phases. For this sample, its corrosion current density and charge transfer resistance are 1.94 μA/cm2 and 1734 Ω•cm2 in NaCl solution respectively, which exhibits obviously improved corrosion resistance in comparison with the Ti-free magnet. The charge transfer resistance has been increased by 45.6 %. The apparently improved corrosion resistance is mainly attributed to the decreased amount of active reaction channels and the enhanced protective effect of TiO2, arising from the increment of Ti-rich precipitates. When the content of Ti dopant exceeds 0.5 wt%, the beneficial effects of Ti are overshadowed by the harmful effect of the density reduction on anti-corrosion performance, and the charge transfer resistance decreased with further increasing the dopant content. The new findings provide a theoretical basis for improving physicochemical properties of NdCeFeB magnet.

Comparison of 35 trace elements content in malignant breast tumors with their content in the normal female mammary gland: Original data and a mini-review

Objective: In many countries, including Russia, breast cancer ranks first in the incidence of cancers in women. The etiology of this disease remains largely unclear, but there is evidence indicating that disturbances in the somatic homeostasis of trace elements may be involved in the process of oncogenesis. Therefore, this study was aimed at identifying changes in the content of trace elements during malignant transformation of breast tissue.Methods: For this purpose, an effective method of small sample analysis by means of inductively coupled plasma mass spectrometry was developed. The method makes it possible to determine the content of 35 trace elements in microsamples (with mass ≥ 10 mg) of breast tissue obtained by puncture biopsy. With the help of this technique, the samples of cancerous (n = 43) and normal (n = 38) breast tissue were studied.Results: In malignant breast tissue, the content of Al, As, B, Cd, Co, Cs, Cu, Mg, Mn, Mo, Ni, Rb, Se, Sr, Ti, Tl, U, V, Zn, and Zr was higher, while the content of Ge, Pb, Sb and Th was lower than in healthy gland tissue. All the identified differences were statistically significant.Conclusions: The significant disruption of somatic homeostasis of trace elements resulting from malignant transformation of breast tissue has been described, but its cause has not been determined, so additional research is required. Further the method we employ, which we have developed and described here, requires tissue samples weighing only a few milligrams, so it is possible to use it with tissue obtained from puncture tissue biopsies.

High-yield rice with rich nutrition and low toxicity can be obtained under potato-rice cropping system.

Rice is often rotated with dryland crops to produce sufficient foodstuff, as rice is the main food crop of humans. In order to verify whether under the intensive rice-based cropping system, high yield and good quality of rice can be achieved simultaneously to ensure food security. Five long-term paddy-upland rotations - wheat-rice (WR), rapeseed-rice (RR), garlic-rice (GR), broad beans-rice (BR) and potato-rice (PR) - were conducted from 2014 to investigate rice yield, along with the profiling of 24 elements in rice grain. Mg, Zn, Cu, As, Mo and Sb concentrations were highest in the aleurone layer, and Ag and Cd concentrations showed little variation among different parts of the rice grain. Al, Ti, V, Si, Fe and Tl concentrations in the endosperm under GR were higher, while the Se concentration under PR was the highest. Furthermore, the yield of GR and PR were higher than the other three rotations with N supplementation, and the sustainable yield index of PR and WR were larger than 0.8. When we consider the concentration of toxic (As, Cd and Pb) and nutrient elements (Ca, Fe, Zn, Se, Cu and Mg) in the endosperm and grain yields, PR can simultaneously achieve high yield, high nutrition and low toxicity with different nitrogen treatments. Here we provide novel insights regarding the selection of rice-based cropping systems, focused on producing nutritious and safe rice with high grain yield. © 2024 Society of Chemical Industry.

Oxidation and ablation resistance of (TiZrHf)C medium-entropy ceramic coating on C/C composite constructed in-situ at low temperature down to 900°C

The low-cost construction of ultra-high temperature high/medium-entropy ceramic coatings is pivotal for advancing their engineering applications. The study successfully prepared (TiZrHf)C medium-entropy ceramic coatings on C/C composite surfaces using an in-situ molten salt disproportionation reaction at temperatures as low as 900°C. The (TiZrHf)C coatings, approximately 20 μm thick, showed uniform distribution of Ti, Zr, and Hf, typical of medium-entropy ceramics. The process entails Hf reducing Zr⁴⁺ and Ti⁴⁺ to divalent states, which then disproportionate and react with carbon to form the coatings. High-temperature oxidation tests revealed larger oxide grain sizes and dense boundaries in coatings with higher Ti content, indicating superior oxidation resistance. Additionally, ablation tests demonstrated that a suitable amount of liquid-phase TiO₂ formed on the composite surface improves ablation resistance by stabilizing the oxide layer. This cost-effective, highly designable method promotes medium/high-entropy ultra-high temperature ceramics' engineering application.

Heavy Metals Distribution in Mangrove Leaves in Various Sudanese Coastal Zones at The Red Sea

<p style="text-align:justify;"><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">Mangrove ecosystem contamination, especially in the Red Sea region, has caused major concerns on a worldwide scale. The heavy metal accumulation typical of a mangrove species, </span><em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">Avicenna marina </span></em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">L. (</span><em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">A. marina</span></em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">) leaves and soluble salts in sediments have not been studied on the Red Sea coast of Sudan.  The present study investigates the two nutrients calcium (Ca) and iron (Fe) and heavy metals such as barium (Ba), titanium (Ti), and strontium (Sr) in the mangrove species </span><em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;">A. marina</span></em><span style="font-family:"Times New Roman",serif;font-size:10.0pt;line-height:107%;"> in the leaves of six different locations in the Red Sea coastal area, as follows: (Hamasyat (HM) Keligo (KG), and Enkfel (EK) of the Gulf of Dunnabeb, and three sites were selected in the south of the Sudanese coast as follows: (Amarat Island (AM), Ibn Abbas Island (BN), and Ras Kassar (RK). The results demonstrate that the maximum calcium (Ca) and iron (Fe) concentrations in mangrove leaves were 35.9 mg/kg and 4.10 mg/kg recorded at RK and AM, respectively, in the south region of the Red Sea. The heavy metal concentrations (mg/kg) vary between different locations. The higher concentration of heavy metals in mangrove leaves increased as Ba was 1.1 mg/kg in the EG north region. While Ti (0.5 mg/kg) and Sr (2.80 mg/kg) higher concentrations were recorded in AM and EK, respectively, in the south area than in the other experimental sites.   Heavy metals and soluble salts in sediments are continuously monitored in mangrove habitats to ensure they keep within allowed limits. These results could be useful as a database for prospective ecological research, preservation efforts, and long-term sustainable management of the Sudanese mangrove ecosystems throughout the Red Sea coastal.</span></p>

From birth to death: The role of upper-crustal thermal maturation and volcanism in porphyry ore formation revealed in the Yerington district

The current race towards greener energy and its intertwined increase in Cu demand imposes the need to find mineralized centers that are economic despite greater depths. To this end, a better understanding of the processes controlling the metal tonnage of porphyry Cu deposits, the main source of Cu, is needed and the focus of current research and debate. This study provides a comprehensive view of the duration of upper-crustal magmatism and its significance in the degree of metal endowment in porphyry Cu deposits using the Yerington batholith, Nevada, USA, as a case study. The Yerington district constitutes an exceptional example of an exposed porphyry Cu system where the plutonic environment that fed the porphyritic dikes is accessible. Combining trace element geochemistry and high-precision geochronology of zircon from all exposed units, we propose that the thermal maturation of the upper crust by a continuum in magmatic activity without significant hiatuses is a key factor in enabling the formation of large porphyry Cu style mineralization. The Yerington magmatic system transitioned from a volcanically active environment with coeval plutonism to a growing upper-crustal magmatic reservoir that fed the porphyritic dikes and associated mineralized centers to then resume its volcanic activity terminating the ore-forming episode. A relatively high volcanic/plutonic ratio characterized the first expressions of Jurassic magmatism in the district from ∼170 Ma with the coeval eruption of the Artesia Lake volcanics and the protracted emplacement of the McLeod Hill pluton. Geochemically, this period recorded distinctive negative Eu anomalies and a gentle increase in Yb/Dy ratios in zircon with decreasing Ti contents over a large range of zircon crystallization temperatures. This persistent magmatism over ∼2 Myr thermally matured the upper crust, enabling the growth of magmatic reservoirs that formed the Bear and Luhr Hill plutons without known volcanic activity for ∼1.3 Myr. Zircon trace element compositions indicate that this transition occurred as a continuum in decreasing negative Eu anomalies and increasing Yb/Dy with decreasing Ti contents and age across the plutonic units, reaching the more evolved signatures and lowest crystallization temperatures in the zircon from porphyry dikes. An increase in the volcanic/plutonic ratio with the eruption of the Fulstone Spring sequence likely terminated the ore-forming potential of the district. Although many other studies have provided important views on the timing and duration of porphyry Cu deposit formation, the link to their plutonic roots has been limited due to their inaccessibility. Therefore, this study offers the first complete picture into the temporal and chemical evolution of an upper-crustal magmatic system and the roles that factors like prolonged magmatism and volcanism play before and after ore formation. We argue that without the thermal maturation of the upper crust, the construction of a long-lived magmatic reservoir would not have been possible, precluding the formation of porphyry Cu deposits. Under this premise, not only the duration of ore-related magmatic activity, but the occurrence of long-lived precursor magmatism might exercise crucial control on the final tonnage of the deposit and should be considered during exploration for new porphyry deposits.

Variation of the Passive Film on Compositionally Concentrated Dual-Phase Al0.3Cr0.5Fe2Mn0.25Mo0.15Ni1.5Ti0.3 and Implications for Corrosion

AbstractThe passive film on a dual-phase Al0.3Cr0.5Fe2Mn0.25Mo0.15Ni1.5Ti0.3 FCC + Heusler (L21) compositionally concentrated alloy formed during extended exposure to an applied potential in the passive range in dilute chloride solution was characterized. Each phase, with its own distinct composition of passivating elements, formed unique passive films separated by a heterophase interface. High-resolution, surface sensitive characterization enabled chemical analysis of the passive film formed over individual phases. The film formed over the L21 phase had a higher concentration of Al, Ni, and Ti, while the film formed over FCC phase was of similar thickness but contained comparatively higher Cr, Fe, and Mo concentrations, consistent with the differences in bulk microstructure composition. The passive film was continuous across phase boundaries and the distribution of passivating elements (Al, Cr, and Ti) indicated both phases were independently passivated. Spatially resolved analysis of the surface chemistry of the dual-phase CCA revealed that the cation with the highest composition in passive film formed on the FCC phase was Cr (52.4 at. pct) and for the L21 phase was Ti (53.1 at. pct) despite the bulk concentration of each element being below 20 at. pct in their respective phases. Al, Cr, and Ti were enriched in both phases within the passive film relative to their respective bulk compositions. In parallel studies, single-phase alloys with compositions representative of the FCC and L21 phases were synthesized to evaluate the corrosion behavior of each phase in isolation. The corrosion behavior of the dual-phase alloy showed passivity evidenced by a pitting potential of 0.615 VSCE in 0.01 M NaCl. The pitting potential and other electrochemical parameters suggested a combination of behaviors of both single-phase samples, suggesting that the global corrosion behavior may be represented by a composite theory applied to phases, their area fractions, and interphase length. However, the interphase in the dual-phase CCA was a local corrosion initiation site and may limit localized corrosion protectiveness. The alloy design implications for optimization of second phase structure and morphology are discussed.

Nanomechanical and bending properties of nickel-titanium orthodontics archwires by depth-sensing indentation

This study aimed to identify the link between alloy microstructures and the nanomechanical properties of different orthodontic archwires containing nickel-titanium (NiTi) by sensing sliced areas. Previous studies have focused on analyzing and contrasting physical properties such as microhardness, elasticity modulus, and resistance; therefore, the trend is to consider microstructural characteristics in detail. Thirty archwire samples from 3 different commercial brands, American Orthodontics (AO), 3M Unitek (3M), and Borgatta, were analyzed through scanning electron microscopy and energy-dispersive x-ray spectroscopy, transmission electron microscopy, atomic force microscopy, Berkovich nanoindentation, and microtensile microscopy to determine their chemical-crystallographic characteristics and nanomechanical and bending characteristics. The identified formulations of AO and 3M had averages of 20 wt%, for Ni and 15.4 wt% for Ti, with lower concentrations for Borgatta. Alloys of Ni and Ti were distributed in different concentrates in the matrix of the archwires. The nanomechanical properties showed high values of the elastic modulus (82.8 ± 3.6 GPa) and hardness (6.4 ± 1.2 GPa) and a minor deformation degree of 0.38% for the AO wires, although the bending strength exhibited the highest values for 3M. No corrosion was observed with a prolonged hydrolytic attack on the surface of any of the wires (0.0-0.5 National Bureau of Standards units). The highest nanomechanical properties and bending characteristics were observed for wires with higher NiTi precipitate contents, which were distributed differently in the alloy overall in the matrix. The nanoindentations sensed in different areas evidenced different mechanical properties for NiTi depending on its concentrations of Ti and enucleations.

Exploring the effect of Ti doping on the friction characteristic of DLC films on the surface of pump plunger in petroleum extraction environments

DLC film is considered to be one of the most promising film materials for improving the abrasion resistance and operation life of pump plungers draw upon its low friction and high hardness, but the friction characteristics and mechanism of the doping element Ti on pump plungers under the petroleum extraction environment are still unclear. In this paper, the friction performance and mechanism of the doping Ti for DLC film on the appearance of the pump plunger under the petroleum extraction environment were investigated at the microscopic scale by using the reactive molecular dynamics. The outcome shows that the Ti-DLC displays a reduction in average friction force of 78.82 % and a decrease in average temperature of 40.33 % in the oil extraction environment, thus improving the abrasion resistance of the pump plunger. Moreover, with the increase of Ti content, the friction will gradually decrease, and significantly low friction behavior can be even materialized without lubrication. It is found that the main reason for the low friction of Ti-DLC film is that the layered structure determined by Ti concentration is formed on the appearance of friction pair, which inhibits the formation of interfacial carbon bond and reduces the shear stress on the contact surface.

The elemental variance between the "rice" and "non-rice" portions of Maifanitum and its health risk assessment

BackgroundMaifanitum, a mineral used in Chinese medicine, was first documented during the Song Dynasty (960-1279). Historical records suggest its multifaceted therapeutic properties, including detoxification and stasis resolution, necrosis removal and tissue regeneration, diuretic and calculi dissolution and prolonging life. The concentration of elements in Maifanitum may vary depending on its origin, different parts, which can affect its effectiveness in different fields of applications. Therefore, the analysis of elements in Maifanitum and the subsequent health risk assessment have been conducted. This provides an important basis for the quality control and application safety of Maifanitum. MethodThe analytical techniques employed in this study are inductively coupled plasma mass spectrometry (ICP-MS) and inductively coupled plasma optical emission spectrometry (ICP-OES), utilized for the quantitative assessment of 60 elements (Refer to Appendix 1) within Maifanitum samples. Based on the test results, chemometric methods are employed to evaluate the characteristics and differences in elemental concentration from different sources and locations. Additionally, a preliminary health risk assessment is conducted for Maifanitum from different origins and various parts. ResultsWe have established a fingerprint of the elements within Maifanitum, demonstrating a commendable level of similarity. The findings from hierarchical cluster analysis（HCA） corroborated with those from principal component analysis (PCA), collectively unveiling a systematic profile of elemental disparities between Maifanitum samples of diverse origins and applications. It also revealed that there are differences in the concentration of Al, Ga, Be, Hf, Na, Sn, Ti, Zr, Gd, Tb, Sr, Pb, Ce, Ba and other elements in different parts of Maifanitum. While Cd, As, and Cu levels in all samples were within the permissible limits as defined by the Chinese Pharmacopeia, Pb concentrations in the majority of samples were found to surpass these standards, albeit slightly in the ''non-rice'' fraction. The assessment of both beneficial and deleterious elements indicates that the ''non-rice'' fraction of Maifanitum possesses superior quality attributes. Moreover, the overall concentration of rare earth elements in Maifanitum is substantially below the established lower threshold for daily human consumption, with no immediate evidence suggesting any adverse health risks. ConclusionThis study provides a basis for the quality control and safety evaluation of Maifanitum in clinical use.

Size distribution, sources and chemistry of ultrafine particles at Barcelona-El Prat Airport, Spain

The rapid expansion of the aviation sector raises concerns about air quality impacts within and around airports. Ultrafine particles (UFP, diameter < 100 nm) are of particular concern due to their potential adverse health effects. In this study, particle number concentrations (PNC), particle number size distribution (PNSD), and other ancillary pollutants such as particulate matter (PM), nitrogen oxides (NOX), black carbon (BC), sulfur dioxide (SO2), ozone (O3), carbon monoxide (CO) and benzene, as well as organic markers and trace elements (in quasi-UFP) were measured at Barcelona-El Prat Airport (80 m and 250 m from the main taxiway and runway). Comparisons were made with an urban background (UB) location, and source apportionment of PNSD was performed using Positive Matrix Factorization (PMF). PNC inside the airport was nine-fold higher than the UB, and fifteen-fold higher when considering only nucleation mode particles (< 25 nm). Six sources contributing to PNC were identified inside the airport: Taxiing (48.7 %; mode diameter = 17 nm), Industrial/Shipping (7.4 %; mode diameter = 35 nm), Diesel (3.9 %; mode diameter = 64 nm), Regional recirculation (1.1 %; mode diameter = 100 nm), Photonucleation (16.6 %; mode diameter = 13 nm) and Takeoff (18.5 %; mode diameter = 23 nm). Due to the measurement location and prevailing wind patterns, no significant contributions from landings were detected. Chemical analysis of quasi-UFP collected on Electrical Low-Pressure Impactor (ELPI + ) filters (stages 2 to 6: 17–165 nm) revealed higher concentrations (> 2-fold) of Fe, Al, Cr, Cu, Mo, Mn, Pb, Ti, and Sb at the airport compared to the UB, with Al exhibiting the most pronounced disparity. Generally, PAH levels were low at both sites, although concentrations were higher at the airport relative to the UB. Overall, this study provides a comprehensive understanding of UFP within a major European airport, identifying the different sources contributing to PNC and PNSD.

Putting advanced materials to the test: Ti3C2 MXenes alleviate the hazardous effects of the environmental pollutant benzo[a]pyrene

Advanced materials are materials that have been engineered to exhibit novel or enhanced properties that confer superior performance when compared to conventional materials. Here, we evaluated the impact of Ti3C2 MXenes, a two-dimensional (2D) material, on the adverse effects caused by polycyclic aromatic hydrocarbons. To this end, we studied benzo[a]pyrene denoted here as B[a]P as a model compound. B[a]P was found to adsorb to MXenes as evidenced by UV-Vis spectroscopy. MXenes in the presence or absence of natural organic matter (NOM) were well tolerated by zebrafish embryos. The uptake (ingestion) of MXenes by zebrafish was determined by quantifying the Ti content using inductively coupled plasma mass spectrometry (ICP-MS) while Raman confocal mapping was applied for the label-free identification of MXenes in situ in exposed zebrafish. The body burden of B[a]P was determined by gas chromatography-mass spectrometry (GC-MS). The potential impact of MXenes on B[a]P triggered aryl hydrocarbon receptor (AhR) induction was assessed by evaluating the induction of downstream genes including cyp1a, and results were validated by using the transgenic zebrafish reporter tg(cyp1a-eGFP). The potential impact of MXenes on the genotoxicity caused by B[a]P was also assessed. MXenes were shown to ameliorate AhR induction and DNA damage caused by B[a]P. This was corroborated by using the human colon-derived cell line HT-29. Taken together, MXenes were found to be non-hazardous and alleviated the adverse effects caused by B[a]P in vitro and in vivo.

Effect of mechanical vibration on microstructure and performance of Fe-based composite coatings fabricated by underwater laser deposition technology

To solve the problem of the uneven composition and poor performance caused by water environment during the underwater laser deposition process, the mechanical vibration assisted underwater laser deposition technology was innovatively proposed, and Fe-based composite layer was successfully prepared. The microstructure, grain type and properties of Fe-based composite layer with and without mechanical vibration were studied and compared. The results showed that the mechanical vibration broke the grain and promoted the formation of more nuclei, which reduced the average grain size by 13.48 %. The solute located in the grain gap was transferred to the liquid molten pool by mechanical vibration, which reduced the Ti content in the intergranular precipitated phase Fe2Ti and made the Fe2Ti from coarse continuous distribution to fine discontinuous distribution. Additionally, the mechanisms of mechanical vibration promoting the performance of the composite were analyzed comprehensively. Compared with the composite without mechanical vibration, the composite with mechanical vibration had good corrosion resistance after 30 days of immersion, and the tribo-corrosion resistance was also improved. With the aid of mechanical vibration, the ultimate tensile strength and elongation of the composite were increased by 11.30 % and 22.08 %, respectively, due to the formation of recrystallized grains, high density high-angle grain boundaries, and fine intergranular precipitate. This study was expected to provide a new way to regulate the microstructure and properties of the underwater laser deposition layer, and promote the application of underwater laser deposition technology in marine engineering equipment.