Laboratory size (5 kg) aluminum killed low carbon steel melts were desulfurized with synthetic fluxes in zirconia crucibles. The sulfur, oxygen, aluminum, silicon and manganese contents in the melt were determined as a function of refining time and temperature. With a good argon shield and synthetic flux cover, melt reoxidation was not observed. Sulfur removal followed first order reaction kinetics. The effectiveness of calcia saturated calcium-aluminate (12CaO·7Al2O3) based fluxes in desulfurizing the steel melts was evaluated. The effects of initial sulfur level of the melt, weight of the flux (slag) and additions of tellurium, fluorspar and barium oxide to the melt on the kinetics of desulfurization were also studied. Résumé Au moyen de flux synthétiques et dans des creusets en zircone, on a désulfré de l'acier fondu à faible teneur en carbone, à une échelle de laboratoire (5 kg). La teneur en soufre, en oxygène, en aluminium, en silicone et en manganese fur déterminée en fonction du temps d'affinage et de la température. Avec une bonne protection à l'argon et une couverture de flux synthétique, on n'a pas observé de réoxydation du matériau fondu. Le retrait du soufre suit une réaction cinétique du premier ordre. On a évalué l'éfficacité des flux à base d'aluminate de calcium saturé d'oxyde de calcium pour désulfurer les aciers fondus. On a aussi étudié les effets sur la cinétique de désulfuration, du niveau initial de soufre, dans les materiaux fondus, de la masse des flux (scories) et de l'addition de tellure, d'oxyde de baryum et de fluorine aux matériaux fondus.