The nuclear magnetic resonance superconducting magnet technology is being developed in our laboratory. Because the upper critical magnetic field of NbTi alloy is not high enough, an Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn superconductor has to be used in the manufacture of magnets for 500 MHz and above. In this paper, an experimental Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn superconducting coil was manufactured to study the fabrication technology. The bobbin with Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ceramic coating is made of stainless steel. A vertical tube type vacuum heat treatment furnace was established for Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn formation. Heat treatment parameters for the Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn coil were done at 670 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">°</sup> C in vacuum. Vacuum pressure impregnation was done to strengthen the assembly. The Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn coil, the switch, and the current leads were joined together using superconducting solder matrix replacement method. In the test the maximum current of the Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn coil was 263 A, corresponding to a central magnetic field of 3.47 T. Persistent current mode operation was also successfully performed.
Read full abstract