Borate based non-centrosymmertic crystals are known for their non-linear optical properties. This study reports BiB3O6 glass-ceramics for photocatalysis and piezocatalysis applications. These were fabricated via. melt-quench technique and yellow transparent glass samples were made. Effectiveness of a bismuth-triborate glass-ceramic (BiB3O6) in degrading methylene blue (MB) and methyl violet (MV) dye undergoing photocatalysis in the presence of visible light and solar light for MB dye was studied. Degradation observed in photocatalysis was ∼62 % and ∼50 % for MB and MV dye respectively in 240 min whereas, ∼72 % of MB dye was degraded under solar light. Piezocatalysis was examined to assess the extended potential of this material, resulting in approximately ∼76 % degradation of MB dye. Moreover, in synergistic photo-piezocatalysis degradation of ∼88 % was observed. Phytotoxicity was also assessed using the germination index (GI) showing ∼76 %, using heat treated sample.