Silorane-based Composite Research Articles

Macro-, micro- and nano-mechanical investigations on silorane and methacrylate-based composites

Objectives Cationic ring-opening monomers with a reduced shrinkage stress – silorane – are being used as matrix resins for recently introduced dental composites. Since shrinkage and mechanical properties are generally opposite properties, our study aimed to analyze the mechanical behavior of the silorane-based composite in comparison to six homologous clinical successful methacrylate-based composites. Methods Mechanical properties were determined at macro- (strength and modulus of elasticity), micro- (hardness, modulus of elasticity and creep) and nano-scale (nano-dynamic-mechanical parameters: complex, storage, loss modulus and tan δ) after storing the materials for 24 h in distilled water as well as after aging (thermocycling and storing for 4 weeks in water, saliva or alcohol). Results The strongest influence on the mechanical properties at macroscopic scale was exerted by the storage media although the influence of the material was also significant. At micro- and nano-scale, the material itself influenced the mechanical properties stronger than the storage. By comparing the four storage conditions, a multivariate analysis revealed a significant decrease in all measured mechanical properties by storing for 4 weeks in water, saliva or alcohol, when compared to the 24 h storage. The strongest effect was exerted through the alcohol storage, whereas the effect of storing for 4 weeks in water or saliva was comparable. The nano-composites were more degraded by a 4-week storage in water and saliva than the micro-hydrids, whereas the effect of storing in alcohol was material depended. The tested silorane-based composite revealed good mechanical properties. The material was very stable in all applied solvents and more reliable by storing in alcohol solutions than the measured methacrylate-based composites. Significance From the point of view of the mechanical properties measured at macro-, micro- and nano-scale, the silorane-based composite was comparable to clinically successful methacrylate-based composite materials, encouraging the clinical use of the new composite material.

Effects of sonic scaling on the surface roughness of restorative materials

The surface roughness of dental restorative materials has a crucial effect on the health of dental and periodontal tissues as well as for the longevity of restorations. In this study we tested a glass ionomer restorative cement, two nanohybrid resin composites, a flowable resin composite and a silorane-based composite. Twenty cylindrical specimens of each material were prepared, cured, polished and instrumented with a sonic scaler (Alegra ST ZE-55 RM W&H, Austria). The mean surface roughness was recorded using a profilometer (SJ-201, Mitutoyo, Japan) at three stages: before scaling, after scaling and after re-polishing. Additional specimens were analyzed by scanning electron microscopy and back-scattered imaging. Data were examined statistically by analysis of variance (ANOVA) and post-hoc tests at a level of significance of P < 0.05. The profilometric measurements and the SEM evaluation showed that, in most of the materials tested, the surface roughness was significantly increased after sonic instrumentation. After re-polishing the specimens, the roughness values were decreased. Periodontal scaling should include polishing of restorations in order to overcome alterations in surface roughness.

Streptococcal adhesion to novel low-shrink silorane-based restorative

Objectives The aim of the present study was to compare the susceptibility of one novel silorane-based and four widely used conventional methacrylate-based resin composites to adhere oral streptococci and to relate any differences to surface roughness, hydrophobicity and type of matrix. Methods Specimens of restoratives Filtek Silorane, Filtek Z250, Tetric EvoCeram, Quixfil and Spectrum TPH were prepared (10.0-mm diameter, 2.0-mm height). Surface roughness was assessed by perthometer measurements and hydrophobicity according to water contact angles was determined by computerized image analysis. Bacterial suspensions of Streptococcus oralis, Streptococcus sanguinis, Streptococcus gordonii and Streptococcus mutans were incubated for 2.5 h at 37 °C with 15 test specimens for each material and adhesion was quantified with fluorescence dye Alamar Blue/Resazurin and an automated multi-detection reader. Glass served as reference. Statistical analysis was performed using the Mann–Whitney U-test ( α = 0.05). Results Median roughness values of all composites ranged between 0.04 and 0.11 μm, median contact angles between 59.7° and 92.1°. Significantly lowest fluorescence intensities of all test materials were found on Filtek Silorane for three of four streptococcal strains. The fluorescence intensities of the four conventional methacrylate resin composites were significantly higher and comparable among each other. Significance When compared against four conventional methacrylate composite resins, a general significance to a lower quantity of adhering streptococci was found on the novel silorane-based composite resin, which might result from its increased hydrophobicity. The low adhesion potential of the silorane-based composite may potentially improve the longevity of direct fillings and reduce recurrent caries.

Properties of silorane-based dental resins and composites containing a stress-reducing monomer

Objective To evaluate properties of silorane-based resins and composites containing a stress reducing monomer. Methods Resin mixtures and composites were formulated containing (a) a developmental stress reducing monomer [TOSU; Midwest Research Institute]; (b) Sil-Mix (3M-ESPE); (c) photo cationic initiator system. Standard BISGMA/TEGDMA resin (B/T) and composite (Filtek Z250) were used as controls. Polymerization volume change was measured using a NIST mercury dilatometer and polymerization stress using an Enduratec mechanical testing machine. Three point bend tests determined flexural elastic modulus, work of fracture, and ultimate strength (ADA 27; ISO 4049). Fracture toughness was measured using ASTM E399-90. Four groups of resins and composites were tested: Sil-Mix, methacrylate standard, and Sil-Mix with two addition levels of TOSU. An ANOVA was used and significant differences ranked using Student–Newman–Keuls test ( α = 0.05). Results Polymerization stress values for resins containing TOSU were significantly less than the other materials. Polymerization shrinkage values for Sil-Mix formulations were significantly less than for B/T, but were not different from each other. TOSU-containing formulations generally had somewhat lower mechanical properties values than Sil-Mix or B/T. Polymerization stress values for Sil-Mix-based composites were significantly less as compared to Z250. The 1 wt.% TOSU composite had the lowest stress. No difference between composite groups was noted for fracture toughness or work of fracture. For ultimate strength, the 5 wt.% TOSU formulation differed significantly from Z250. All Sil-Mix formulations had elastic modulus values significantly different from Z250. Significance The ability of TOSU to reduce polymerization stress without a proportional reduction in mechanical properties provides a basis for improvement of silorane-based composites.