Shrinkage Of Ultra-high Performance Concrete Research Articles

Effects of Shrinkage Reducing Agent and Expansive Admixture on the Volume Deformation of Ultrahigh Performance Concrete

This paper investigated the influences of shrinkage reducing agent and expansive admixture on autogenous and drying shrinkage of ultrahigh performance concrete (UHPC) containing antifoaming admixture. The shrinkage reducing agent was used at dosage of 0.5%, 1%, and 2% and the expansive admixture was used at dosage of 2% to 4% by mass of cementitious material. The results show that the air content of UHPC increases with the higher addition of shrinkage reducing agent and expansive admixtures. However, the fluidity, compressive strength, and shrinkage of UHPC exhibit a declining tendency. The usage of expansive agent at dosage of 4% significantly reduces the shrinkage of UHPC. The 7-day autogenous shrinkage was decreased by 16.0% and 28-day drying shrinkage was decreased by 29.5%, respectively. Shrinkage reducing agent at dosage of 2% reduced the 7-day autogenous shrinkage by 44.3% and 28-day drying shrinkage by 50.2%. Compared with expansive admixture, shrinkage reducing agent exhibits more efficient shrinkage reduction effect on UHPC.

Effectiveness of Saturated Coral Aggregate and Shrinkage Reducing Admixture on the Autogenous Shrinkage of Ultrahigh Performance Concrete

The use of saturated coral aggregate (SCA) as practical replacement of quartz sand has been shown to effectively mitigate the autogenous shrinkage in ultrahigh performance concrete (UHPC). The autogenous deformation, the compressive strength, the flexural strength, and the hydration property development of paste with different shrinkage means were tested. Three different methods were evaluated to mitigate the autogenous shrinkage: SCA, shrinkage reducing admixture (SRA), and the mixture of SCA and SRA (SRA-SCA). It was found that SCA and SRA have all the effective ways to reduce the shrinkage deformation, and SRA-SCA was the most effective in mitigating the shrinkage. The autogenous shrinkage of UHPC was restrained, when the SCA dosage was 44%, the SRA dosage was 0.8%, the SCA content was 26%, the SRA dosage was 2.4%, the SCA content was 18%, the SRA content was 2.4%, or the SCA dosage was 26%. The mechanical properties were deteriorated by the addition of SCA, while the compressive strength was still higher than 90 MPa at 28 days even though the replacement ratio of SCA was up to 50%. Furthermore, internal curing by means of SCA was proved to be a successful way to mitigate autogenous shrinkage, after the tests.

Early-age shrinkage development of ultra-high-performance concrete under heat curing treatment

The effects of a novel heat curing regime and longitudinal reinforcement ratio on early-age shrinkage of ultra-high performance concrete (UHPC) were experimentally investigated in this study. The microstructure, porosity and calcium hydroxide (CH) content of UHPC after different heat curing durations were characterized with scanning electron microscopy, mercury intrusion porosimetry and thermal analysis. The results indicate that slight shrinkage was observed when the heat curing duration was less than 60min and curing temperature reached 48°C. However, when the heat curing duration approached 70min and curing temperature was around 55°C, the early-age shrinkage increased dramatically. It was found that the early-age shrinkage is approximately 450με after 48h of heat curing. The results also show that the early-age shrinkage of UHPC significantly decreased by percentage of 33–60% with the increase of longitudinal steel reinforcement ratio from 2.0 to 4.52%. Meantime, after 10h of heat curing, the cement hydration and secondary hydration in UHPC tend to finish, which consequently leads to dense microstructure and low CH content in UHPC.

Effect of supplementary cementitious materials on autogenous shrinkage of ultra-high performance concrete

Ultra-high performance concrete (UHPC) not only presents ultra-high compressive strength but also exhibits ultra-high durability, due to its extremely dense structure and consequently highly reduced porosity. However, high dosages of silica fume (SF), typically adopted in UHPC, also lead to high autogenous shrinkage. This phenomenon, occurring at early ages, induces high internal stresses that, in turn, cause microcracking and increase permeability and, therefore, reduce the durability of concrete structures. The experimental study was conducted aiming to replace SF by another fine supplementary cementitious materials (SCMs), such as fly ash (FA) or ground granulated blast furnace slag (GGBS), in order to reduce the amount of autogenous shrinkage. The adopted approach involved partial or total replacement of SF by SCMs. Results indicate that the amount of fine pores in UHPC is a predominant factor that can highly affect the autogenous shrinkage. A strong correlation between the natural logarithm of autogenous shrinkage and the total porosity of UHPC mixtures was established. It was found that reducing the amount of fine pores in specimens containing FA or GGBS leads to a reduction of the autogenous shrinkage.

Evaluation of Setting Time in Ultra High Performance Concrete

Ultra high performance concrete (UHPC), characterized by a high strength and high ductility, is also subjected to large shrinkage due to its low water-to-binder ratio and its large content in high fineness materials. The large amount of autogenous shrinkage of UHPC can induce crack on structural member when it was restrained with reinforcement and form. However, shrinkage of UHPC in plastic state is not generating confining stress, which is the main cause of initial crack. Normally, the setting time in concrete is an index to distinguish shrinkage which occur confining stress or not. An estimation of setting time is conducted in compliance with ASTM C 403 till now however, that test standard reveals error of results due to discordance of test condition as following with concrete type. This study therefore evaluated setting time of UHPC through the modified test method which was proposed by KICT. Test results and analyses proved a discrepancy of setting time between ASTM and proposed method. The proposed method put faith in evaluation of setting time in accordance with UHPC.

An Evaluation on the Restrained Shrinkage of Ultra-High Performance Concrete

Since ultra-high performance concrete (UHPC) is subject to large occurrence of shrinkage at early age due to its low water-to-cement ratio, the mixing of large quantities of powdered admixtures and the absence of coarse aggregates, UHPC presents large risks of shrinkage cracking caused by the restraints provided by the form and reinforcing bars. Accordingly, this study intends to evaluate the shrinkage behavior of UHPC under restrained state by performing restrained shrinkage test using ring-test. The test results reveal that increasing thickness of the inner ring increases the tensile creep at early age leading to the reduction of the average strain and residual stress of the inner ring.

The Influence of Chemical Admixtures on the Autogenous Shrinkage Ultra-High Performance Concrete

Ultra-high performance concrete (UHPC) is a material developing remarkable performance with compressive strength of about 200 MPa and flexural strength of approximately 30 MPa on which research is actively conducted today. However, UHPC is also characterized by a mixing composed of a high specific quantity of binder that is a W/B ratio of about 0.2, which requires to examine the effects of the autogenous shrinkage. Accordingly, this study investigates the effects of the use of expansive additive and water reducing agent on the autogenous shrinkage of UHPC at early age. To that goal, autogenous shrinkage test and ultrasonic pulse velocity (UPV) monitoring are conducted for a mixing of UHPC using expansive additive and shrinkage reducing agent. The experimental results reveal that the autogenous shrinkage of UHPC reduces by 24% for a mix of UHPC adopting both 7.5% of expansive additive and 1% of shrinkage reducing agent compared to the mix without admixture. Furthermore, this mix is seen to compensate the autogenous shrinkage occurring at early age when UHPC develops its largest stiffness in view of the UPV evolution curve. At that time, the shrinkage stress seems to be extremely softened.

Effect of drying conditions on autogenous shrinkage in ultra-high performance concrete at early-age

This experimental study investigated the effects of drying conditions on the autogenous shrinkage of ultra-high performance concrete (UHPC) at early-ages. UHPC specimens were exposed to different temperatures, namely, 10, 20 and 40°C under a relative humidity (RH) ranging from 40 to 80%. The effects of using a shrinkage-reducing admixture (SRA) and a superabsorbent polymer (SAP) as shrinkage mitigation methods were also investigated. The results show that autogenous and drying shrinkage are dependent phenomena. Assuming the validity of the conventional superposition principle between drying and autogenous shrinkage led to overestimating the actual autogenous shrinkage under drying conditions; the level of overestimation increased with decreasing RH. Both SRA and SAP were very effective in reducing autogenous shrinkage under sealed conditions. However, SRA was efficient in reducing drying shrinkage under drying conditions, while SAP was found to increase drying shrinkage. Generally, results indicate that adequate curing is essential for reducing shrinkage in UHPC even when different shrinkage mitigation methods are applied.

Short-term tensile creep and shrinkage of ultra-high performance concrete

The tensile creep and free shrinkage deformations of ultra-high performance concrete (UHPC) were examined through short-term testing to assess the influences of stress/strength ratio, steel fiber reinforcement, and thermal treatment. The use of fibers and the application of thermal treatment decreased 14-day drying shrinkage by more than 57% and by 82%, respectively. Increasing the stress-to-strength ratio from 40% to 60% increased the tensile creep coefficient by 44% and the specific creep by 11%, at 14 days of loading. Incorporating short steel fibers at 2% by volume decreased the tensile creep coefficient by 10% and the specific creep by 40%, at 14 days. Also, subjecting UHPC to a 48-h thermal treatment at 90 °C, after initial curing, decreased its tensile creep coefficient by 73% and the specific creep by 77% at 7 days, as compared to ordinarily cured companion mixes. Comparison of tensile creep behavior to published reports on compressive creep in UHPC reveal that these phenomena differ fundamentally and that further evaluation is necessary to better understand the underlying mechanisms of tensile creep in UHPC. Results from this study also showed that the effects of both thermal treatment and fiber reinforcement were more pronounced in tensile creep behavior than tensile strength results of different UHPC mixes. This emphasizes the importance of conducting tensile creep testing to predict long-term tensile performance.