Scotchbond Universal Research Articles

Microshear Bond Strength of Scotchbond Universal Adhesive to Primary and Permanent Dentin: A Six-Month in Vitro Study.

Objectives:This study aimed to assess the microshear bond strength (MSBS) of Scotchbond Universal adhesive, used in self-etch and etch-and-rinse modes, to primary and permanent dentin at 24 hours and six months.Materials and Methods:A total of 88 composite micro-cylinders were divided into eight groups (n=11) as follows: (A) Etch-and-rinse, 24 hours, primary dentin; (B) Self-etch, 24 hours, primary dentin; (C) Etch-and-rinse, six months, primary dentin; (D) Self-etch, six months, primary dentin; (E) Etch-and-rinse, 24 hours, permanent dentin; (F) Self-etch, 24 hours, permanent dentin; (G) Etch-and-rinse, six months, permanent dentin; (H) Self-etch, six months, permanent dentin. The MSBS was measured by a testing machine at a crosshead speed of 0.5 mm/minute. Data were analyzed using three-way analysis of variance (ANOVA).Results:The mean MSBS was 12.3±2.3 MPa in A, 18.8±4.1 MPa in B, 11.9±3.7 MPa in C, 16±2.9 MPa in D, 19.1±2.7 MPa in E, 22.8±4.1 MPa in F, 16.2±2.6 MPa in G, and 17.2±4.4 MPa in H. In the self-etch mode, the MSBS was significantly higher than that in the etch-and-rinse mode (P<0.001). The MSBS in permanent teeth was significantly higher than primary teeth (P<0.001). At six months, the MSBS significantly decreased in all groups (P<0.001).Conclusion:The micro-shear bond strength of Scotchbond Universal adhesive decreases over time and depends on the type of tooth and the mode of application of the adhesive.

Etch-and-rinse vs self-etch mode for dentin bonding effectiveness of universal adhesives.

In this study, dentin bond fatigue resistance and interfacial science characteristics of universal adhesives through etch-and-rinse and self-etch modes were investigated. Resin composite was bonded to human dentin with four universal adhesives, namely, Adhese Universal, All-Bond Universal, G-Premio Bond, and Scotchbond Universal Adhesive. The initial bond strengths, bond fatigue strengths, and interfacial science characteristics of the universal adhesives with dentin through etch-and-rinse and self-etch modes were determined. Bond fatigue resistance (initial bond strength and bond fatigue strength) of universal adhesives in etch-and-rinse mode showed no significant difference in contrast to that in self-etch mode and was material-dependent regardless of the etching mode. Although phosphoric acid conditioning of dentin did not have a strong impact on the bond fatigue resistance, surface free energy and parameters of dentin were significantly decreased by etching and by application of universal adhesives regardless of etching mode. Changes in γS and γSh for when universal adhesive was applied to etched and ground dentin were significantly different depending on the adhesive. The results suggest that bonding performance of universal adhesives was effective in both etching modes; however, bonding mechanisms may be different for each.

Impact of Recently Developed Universal Adhesives on Tensile Bond Strength to Computer-aided Design/Manufacturing Ceramics.

The aim of this investigation was to test the tensile bond strength (TBS) between different computer-aided-design/manufacturing (CAD/CAM) ceramics after conditioning using different universal adhesive systems and resin composite cement. Substrates of four CAD/CAM ceramics-1) VITABLOCS Mark II, 2) Initial LRF, 3) Celtra Duo, and 4) IPS e.max CAD (N=648, n=162)-were fabricated. VITABLOCS Mark II and Initial LRF were etched using 9% hydrofluoric acid for 60 seconds, Celtra Duo for 30 seconds, and IPS e.max CAD for 20 seconds. Substrates for conditioning using Monobond Etch & Prime were untreated. The following adhesive systems were used: All-Bond Universal (ABU), Clearfil Universal Bond (CUB), G-Multi Primer (GMP), iBond Universal (IBU), Monobond Etch & Prime (MEP), Monobond Plus (MBP), One Coat 7 Universal (OCU), Prime&Bond Active (PBA), and Scotchbond Universal (SBU). Conditioned substrates were bonded using a resin composite cement (Variolink Esthetic DC), thermal cycled (20,000×, 5°C/55°C), and TBS was measured using a universal testing machine. Data were analyzed using univariate analysis with partial eta-squared, Kolmogorov-Smirnov, Kruskal-Wallis, Mann-Whitney U, and Spearman-Rho tests (α=0.05). ABU, MEP, and MBP obtained the significantly highest TBS, while CUB, IBU, and OCO resulted in the lowest, regardless of the CAD/CAM ceramic. SBU showed varying TBS results depending on the CAD/CAM ceramic used. ABU, MEP, and MBP showed no impact of CAD/CAM ceramic on TBS values. ABU, GMP, MEP, and MBP showed predominantly cohesive failure types in luting composite, while CUB and OCU demonstrated adhesive failure types.

Effects of silver diammine fluoride on bond strength of adhesives to sound dentin.

This study evaluated bonding of adhesives to dentin treated with silver diammine fluoride (SDF). Micro-shear bond strength (MSBS) to sound human dentin was investigated for 3 adhesive systems: Clearfil SE bond 2 (CSE), and Scotchbond Universal in self-etching (SBU) and phosphoric acid-etching (SBT) modes, following 4 different SDF application protocols (n=10); Control: treated with deionized water. P1: SDF applied for 10-s, no rinse. P2: SDF applied for 10-s, rinsed off after 1-min. P3: superficial dentin polished off after 24-h following P1. MSBS data were obtained after 24-h water storage at 37°C. SDF significantly affected MSBS to dentin depending on the SDF protocol and adhesive system. Rinsing SDF off improved bond strength but superficial refreshing of SDFtreated dentin prior to bonding showed the highest bond strength. The two-step self-etch adhesive (CSE) and the universal adhesive in acid-etching mode (SBT) showed better performance than universal adhesive (SBU) alone on SDF treated dentin.

Microtensile Bond Strength of Composite to Enamel Using Universal Adhesive with/without Acid Etching Compared To Etch and Rinse and Self-Etch Bonding Agents.

AIM:Considering the recent introduction of universal adhesives and the controversy regarding the use/no use of etchant prior to their application, this study sought to assess the microtensile bond strength of composite to enamel using universal adhesive with/without acid etching compared to three-step etch and rinse, two-step etch and rinse and two-step self-etch bonding agents.METHODS:This in vitro, an experimental study was conducted on 80 extracted sound human molars in five groups (16 each): Scotchbond Universal adhesive (3M) with/without prior etching, Adper Scthe otchbond Multi-Purpose, Single Bond and Clearfil SE Bond. Etching was performed with 37% phosphoric acid for 20 seconds followed by rinsing and drying. The bonding agent was then applied and light-cured. The e-lite composite was bonded to surfaces and light-cured. The teeth were then mounted, sectioned and subjected to microtensile bond strength test in a universal testing machine. The mode of failure was, determined under a stereomicroscope. Data were analysed using one-way ANOVA followed by Tukey’s test.RESULTS:Universal adhesive with prior etching yielded the highest bond strength (P = 0.03). Pairwise comparisons showed that the bond strength of this group was significantly higher than that of universal adhesive without prior etching (P = 0.04). No other significant differences were noted (P > 0.05). The modes of failure were significantly different among the groups (P = 0.003).CONCLUSION:Enamel etching with phosphoric acid can significantly increase the bond strength to universal adhesive. Universal adhesive without prior etching provided the bond strength as high as that provided by etching and rinse and self-etch bonding agents.

Composite-composite Adhesion as a Function of Adhesive-composite Material and Surface Treatment.

To evaluate the composite-to-composite repair interfacial fracture toughness (iFT) as a function of adhesive and composite repair material. Beam-shaped composite specimens (21×4×3±0.2 mm) were prepared for each substrate material (Filtek Supreme Ultra [FSU] or Clearfil Majesty ES-2 [CME]) and artificially aged for 50,000 thermocycles (5-55°C, 20-second dwell time). Aged specimens were sectioned in half, and the resulting hemispecimens were randomly assigned to one of the different repair methods (n=10) based on the following variables: type of substrate composite (FSU or CME), acid etch (yes or no), adhesive type (Scotchbond Universal or Clearfil SE Bond 2), and type of repair composite (FSU or CME). The repair surface was prepared with a course diamond bur (Midwest #471271). When used, 37% phosphoric acid was applied for 20 seconds, rinsed, and dried. All adhesives and composites were applied according to manufacturers' instructions. After postrepair storage (100% humidity, 37°C, 24 hours), iFT was measured and expressed as MPa. Data were analyzed for statistical significance using a three-way analysis of variance and Tukey post hoc tests (α=0.05). iFT values ranged from 0.64 ± 0.19 MPa to 1.28 ± 013 MPa. Significantly higher iFT values were achieved when FSU was used as the repair composite resin regardless of the substrate composite resin (p<0.001). Clearfil SE Bond 2 adhesive was associated with significantly higher iFT values for FSU substrate (p<0.001). The etching procedure had no significant effect on the iFT values of the repair procedures (p>0.05). Composite repair strength is adhesive and composite dependent. Repair strength appears to be higher when FSU is the repair composite regardless of the adhesive used.

Benefits of Nonthermal Atmospheric Plasma Treatment on Dentin Adhesion.

This study aimed to evaluate the influence of two nonthermal atmospheric plasma (NTAP) application times and two storage times on the microtensile bond strength (μTBS) to dentin. The influence of NTAP on the mechanical properties of the dentin-resin interface was studied by analyzing nanohardness (NH) and Young's modulus (YM). Water contact angles of pretreated dentin and hydroxyapatite blocks were also measured to assess possible alterations in the surface hydrophilicity upon NTAP. Forty-eight human molars were used in a split-tooth design (n=8). Midcoronal exposed dentin was flattened by a 600-grit SiC paper. One-half of each dentin surface received phosphoric acid conditioning, while the other half was covered with a metallic barrier and remained unetched. Afterward, NTAP was applied on the entire dentin surface (etched or not) for 10 or 30 seconds. The control groups did not receive NTAP treatment. Scotchbond Universal (SBU; 3M ESPE) and a resin-based composite were applied to dentin following the manufacturer's instructions. After 24 hours of water storage at 37°C, the specimens were sectioned perpendicular to the interface to obtain approximately six specimens or bonded beams (approximately 0.9 mm2 in cross-sectional area) representing the etch-and-rinse (ER) approach and another six specimens representing the self-etch (SE) approach. Half of the μTBS specimens were immediately loaded until failure, while the other half were first stored in deionized water for two years. Three other bonded teeth were selected from each group (n=3) for NH and YM evaluation. Water contact-angle analysis was conducted using a CAM200 (KSV Nima) goniometer. Droplet images of dentin and hydroxyapatite surfaces with or without 10 or 30 seconds of plasma treatment were captured at different water-deposition times (5 to 55 seconds). Two-way analysis of variance revealed significant differences in μTBS of SBU to dentin after two years of water storage in the SE approach, without differences among treatments. After two years of water aging, the ER control and ER NTAP 10-second groups showed lower μTBS means compared with the ER NTAP 30-second treated group. Nonthermal atmospheric plasma resulted in higher NH and YM for the hybrid layer. The influence of plasma treatment in hydrophilicity was more evident in the hydroxyapatite samples. Dentin hydrophilicity increased slightly after 10 seconds of NTAP, but the difference was higher when the plasma was used for 30 seconds. Dentin NTAP treatment for 30 seconds contributed to higher μTBS after two years of water storage in the ER approach, while no difference was observed among treatments in the SE evaluation. This result might be correlated to the increase in nanohardness and Young's modulus of the hybrid layer and to better adhesive infiltration, since dentin hydrophilicity was also improved. Although some effects were observed using NTAP for 10 seconds, the results suggest that 30 seconds is the most indicated treatment time.

The sonic application of universal adhesives in self-etch mode improves their performance on enamel

The objective of this study was to evaluate the effect of sonic application of universal adhesives on the enamel microshear bond strengths (µSBS), in situ degree of conversion (DC) and etching pattern. Ninety-six extracted third molars were sectioned in four parts (buccal, lingual, proximal) and divided into 12 groups, according to the combination of 1) adhesive system (All-Bond Universal [ABU], G-Bond Plus [GBP], Prime&Bond Elect (PBE), and Scotchbond Universal Adhesive [SBU]), and 2) adhesive application mode (manual active etch-and-rinse [M-ER], manual active self-etch [M-SE], and sonic vibration self-etch [S-SE]). Specimens were stored in water at 37 °C during 24 h and tested at 1.0 mm/min (µSBS). DC was evaluated in the enamel-resin interfaces using micro-Raman spectroscopy. The enamel-etching pattern was evaluated under a field- emission scanning electron microscope. Data were analyzed with two-way ANOVA and Tukey's test (α = 0.05). S-SE application increased µSBS and DC for all universal adhesives when compared to M-SE (p < 0.05). S-SE application resulted in mean bond strengths that were statistically similar to those obtained with the respective ER application mode (p > 0.05). A deeper enamel-etching pattern was observed for all universal adhesives in the etch-and-rinse strategy. An improvement in etching ability was observed in S-SE application compared to M-SE application. In light of the improved performance of universal adhesives when applied sonically in SE mode, selective enamel etching with phosphoric acid may not be crucial for their adhesion to enamel. The sonic application of universal adhesives in self-etch mode may be a practical alternative to enamel etching.

Effect of air-blowing time and long-term storage on bond strength of universal adhesives to dentin.

To evaluate the effects of air-blowing time and storage time on microtensile bond strength (μTBS) of universal adhesives to dentin. Ninety flat dentin surfaces from extracted human third molars were bonded with three universal adhesives (Clearfil Universal Bond-CU; G-Premio Bond-GP; Scotchbond Universal Adhesives-SB). Bonded dentin surfaces were air-dried for 5s, 15s, or 30s followed by resin composite built-up. Resin-dentin beams were tested with μTBS test after different storage time in distilled water (24h and 1year). Data were analyzed by three-way ANOVA and Duncan test at (α = 0.05). Failure mode and resin-dentin interfaces were observed using a scanning electron microscope (SEM). Specific features of fractured beams after μTBS were further observed using SEM at high magnification. Extension of air-blowing time from 5s to 30s increased the 24h μTBS of CU only. Bond strength of all adhesives significantly decreased after 1-year storage except for CU at 5s and 30s of air-blowing time. One-year μTBS were significantly higher when air-blowing times were extended to 15s for SB and 30s for CU. Air-blowing time had no influence on GP. The effect of air-blowing time and storage time on resin-dentin bond was material-dependent. Extended air-blowing time increased the bond strength and bond durability of CU. Extension of air-blowing time to 15s and 30s improve the long-term bond strength of SB and CU, respectively.

Shear bond strength and interface analysis between a resin composite and a recent high-viscous glass ionomer cement bonded with various adhesive systems.

This study investigated the shear bond strength (SBS) and interface between a resin composite and a new high-viscous glass ionomer cement (HV-GIC), a HV-GIC, a resin-modified glass ionomer cement (RM-GIC), a bulk-fill flowable composite, and a regular flowable composite bonded with various adhesive systems. A resin composite (Filtek Z350) was bonded to a new HV-GIC (EQUIA Forte Fil) using various adhesive systems, including a universal adhesive in self-etch and etch-and-rinse mode (Scotchbond Universal), a two-step etch-and-rinse adhesive (Scotchbond 1-XT), a one-step self-etch adhesive (Optibond All-in-one) tested also after silane application (Monobond Plus), and a coating material (EQUIA Forte Coat). The resin composite was also bonded to a HV-GIC (Fuji IX GP), a RM-GIC (Fuji II LC), a bulk-fill flowable composite (SDR), and a regular flowable composite (Tetric Evo Flow) with the universal adhesive in self-etch mode (Scotchbond Universal). Two-way ANOVA followed by Dunnett's post hoc test was used to investigate the difference in SBS. Failures were analyzed by chi-square test. Bonding interfaces were examined by environmental scanning electron microscopy (E-SEM). SBS to EQUIA Forte Fil was significantly lower with Scotchbond 1-XT than with all other adhesive systems. By using Scotchbond Universal with the self-etch technique, the SBS to EQUIA Forte Fil was significantly higher than the SBS to Fuji IX GP and significantly lower than the SBS to Fuji II LC, SDR, and Tetric Evo Flow. E-SEM images showed an intimate contact at all interfaces examined. EQUIA Forte Fil showed satisfactory SBS and interfaces with all adhesives tested. Bonding between the resin composite and HV-GIC can be achieved using a universal adhesive in self-etch mode, an easy-to-use adhesive system.

Analysis of pre-test failures and bond-strengths of seven adhesive systems to bovine dentine: A nine-year novice/beginner operator study

ObjectiveThe aims were to evaluate, via multi-year student cohorts: (i) the incidence of pre-test failures and (ii) shear bond strengths of single- and multi-step adhesives to bovine dentin. MethodsThe experiments were performed by cohorts of dental students (2008–2016). Each year the bond strengths of three dental adhesives to bovine dentin were tested. Four self-etching adhesives (Optibond-All-in-One, [OBAIO]; Optibond XTR [OBXTR]); Xeno V [XV]; Xeno V+ [XV+]; a three-step etch-and-rinse-system (Optibond FL, [OBFL]), a self-etch universal adhesive (Scotchbond Universal [SBU]) and a self-etch/etch-and-rinse adhesive (Xeno Select, [XS]) were included in the study. Composite-cylinders were bonded perpendicularly to prepared bovine dentin surfaces. Shear-tests were performed with a universal-testing-machine. ResultsBoth overall, and within years, XV and XV+ showed significantly (p<0.01) higher percentages of pre-test failures versus other adhesive systems tested in the period 2008–2014 (OAIO, OBFL, OBXTR). Fewest pre-test failures were observed for OBFL, OBXTR and SBU. Trends in mean bond strengths and Weibull distributions were noted, per adhesive, with trends in the incidence of pre-test failures. Pre-test-failures and bond strengths depended on the air-drying technique. The adhesive systems showed variable technique sensitivity.Multistep bonding systems (Optibond FL and Optibond XTR) showed minimal pre-test failures and high bond strength applied by relatively inexperienced operators and irrespective of the applied air-drying technique. However, two single-step adhesives (OAIO and SBU) showed comparable results to the multi-step systems. SignificanceThe clinical need for rapid application dentine adhesives can result in varied outcomes with relatively inexperienced operators. These outcomes include both the incidence of pre-test failures as well as the distributions of shear bond strengths achieved, although these measures appear to be related. However, both outcomes are dependent upon the adhesive products utilised and especially upon the applied air pressure (flow rate). Some rapid application systems appear to perform comparably with well-established multi-step adhesives.

In-vitro performance of CAD/CAM crowns with insufficient preparation design

PurposeTo compare the debonding and fracture force of different CAD/CAM composite crowns with respect to the influence of water storage (0d vs. 90d/37 °C) and types of cementation (adhesive vs. self-adhesive). MethodsExtracted human molars were prepared with a worst-case preparation scenario providing a nonretentive design (height ~4 mm; angle ~15°) and reduced fitting (250 µm). After digitalization, 72 crowns (n = 8 per group; circular wall thickness 1.5 mm / occlusal thickness ~2.5 mm) were milled from the composites (CS, LU), one experimental composite (EX), a resin-infiltrated ceramic (VE), and a feldspar ceramic reference (VM). The crowns were adhesively bonded (Scotchbond Universal + Rely X Ultimate, 3M), and two groups (EX, VE) were additionally cemented with a self-adhesive cement (RelyX Unicem, 3M). After 90-d water storage, thermal cycling and mechanical loading (TCML) were performed. Restorations, which failed during storage or TCML, were analyzed using scanning electron microscopy, and surviving restorations were loaded to fracture. To evaluate storage effects, two materials (EX, LU) were investigated without water storage. ResultsCS (7×) and LU (2×) exhibited debonding during 90-d storage. LU (5×) debonded during TCML. Cement remained on the inner sides of the crowns in all cases. EX and VE survived storage and TCML without failure or debonding. Two specimens of VM exhibited cracks after TCML. Fracture forces varied between 720 N and 2155 N. Solely the results between VE and VM were not significantly different (p = 0.204). Debonding effects due to water storage were material dependent. Fracture forces in tendency (p > 0.117) were higher for self-adhesive cementation. ConclusionsDebonding and stability of CAD/CAM crowns were material dependent. Water storage affected debonding, and cementation marginally influenced performance and fracture force.

Effects of bond strength evaluation on different durations of adult permanent teeth and youth permanent teeth by using universal adhesives to dentin

To compare the dentin bonding strength evaluation between adult permanent teeth and youth permanent teeth after treatment for different durations by universal adhesives. Ten adult permanent teeth and ten youth permanent teeth were selected for this study. The occlusal enamel layer was removed, and each tooth was cut into three pieces along the long axis. In total, 30 pieces of adult and youth teeth were prepared. The adult and youth teeth pieces were randomly divided into three groups and treated by universal adhesives for 10, 20, and 30 s. In this study, Scotchbond Universal (SBU) was selected as the universal adhesive. Slabs were treated by dual-cure resin cements. The specimens were tested by microshear strength test through a universal testing machine. Fracture modes were observed by a stereomicroscope. Other adult teeth and youth teeth were selected, two for each type, and treated and grouped in the same manner. Fluorescein (0.1% Rhodamine B) was dissolved in SBU adhesive, and the specimens were treated by the adhesives for 10, 20, and 30 s. Micromorphology of the resin protrusions on the adhesive surface was observed by laser confocal microscopy (CLSM). For the adult teeth, the highest micro-shear bonding strength was observed in the 20 and 30 s groups, and the values were higher than that of the 10 s group (P<0.05). For the youth teeth, the highest micro-shear bonding strength was observed in the 10 and 20 s groups, and the values were higher than that of the 30 s group (P<0.05). The micro-shear bonding strength in the 10 s youth teeth group was higher than that of the 10 s adult teeth (P<0.05) and was same as the adult teeth treated for 20 s (recommendation time of material instructions) (P>0.05). The main break patterns in different groups comprised adhesive failure fractures and several mixed failure fractures. No resin fracture mode was observed. CLSM revealed very few short resin protrusions in 10 s adult teeth group, whereas the number and length of resin protrusions significantly increased in the 20 s adult teeth group. The resin protrusions of the 30 s group were shorter than those of the 20 s adult teeth group. In different durations, the bonding interface in different youth teeth groups presented the same trend of change as the adult teeth. However, the number and length of resin protrusions in the 10 s group of youth teeth were all higher than those of the 10 s adult teeth group. In clinical practice, the bonding agent treatment duration shall be shortened appropriately for youth permanent teeth, and that for adult permanent teeth shall not be shortened to less than 20 s. On the whole, the bond strength of youth permanent teeth can achieve no significant difference with the adult permanent teeth.

Effect of MDP-Based Primers on the Luting Agent Bond to Y-TZP Ceramic and to Dentin.

Purpose The aim of this study was to evaluate the influence of multimode MDP-based primers and different application protocols on the bond strength of a representative resin cement to an yttrium stabilized tetragonal zirconia (Y-TZP) ceramic. Materials and Methods The occlusal dentin from 60 human molars was exposed. The teeth and zirconia cylinders (N = 60) (3 mm of diameter; 4 mm of height) were divided into six groups (n = 10) according to the ceramic surface conditioning: (1) air abraded with SiO2 particles; (2) Z-Prime Plus; (3) air abraded with SiO2 particles + Z-Prime Plus; (4) air abraded with SiO2 particles + All-Bond Universal; (5) air abraded with SiO2 particles + ScotchBond Universal Adhesive; and (6) untreated zirconia. The luting agent (Duo-Link cement) was applied on the treated dentin surface. Specimens were stored in water (37°C, 24 h) and tested in shear bond strength. Data were statistically analyzed using 2-way ANOVA and Post hoc Tukey tests (α = 0.05). Results Significant effects of ceramic conditioning were found (p < 0.0001). The specimens sandblasted with silica particles followed by the application of Z-Prime Plus or All-Bond Universal presented greater bond strength values. For the untreated zirconia, several specimens failed prematurely prior to testing. Conclusions Sandblasting with silica particles combined with Z-Prime Plus increased the bond strength.

Effect of Different Adhesive Strategies and Time on Microtensile Bond Strength of a CAD/CAM Composite to Dentin.

The aim of this study was to evaluate the effect of adhesive strategy and time on the microtensile bond strength of a computer-aided design/computer-aided manufacturing (CAD/CAM) composite to dentin. Sixty CAD/CAM composite blocks were bonded to human dentin with simplified bonding agents using etch-and-rinse and self-etching approaches and amine-based and amine-free resin cements, with and without the application of a dual-cure activator (DCA; n=10): SBP-ARC (Adper Single Bond Plus + RelyX ARC), SBP-RXU (Adper Single Bond Plus + RelyX Ultimate), SBP-DCA-RXU (Adper Single Bond Plus + DCA + RelyX Ultimate), SBU-ARC (Scotchbond Universal + RelyX ARC), SBU-RXU (Scotchbond Universal + RelyX Ultimate), and SBU-DCA-ARC (Scotchbond Universal + DCA + RelyX ARC). Each specimen was light cured for 40 seconds under load and stored in distilled water at 37°C for seven days. Stick-shaped specimens (1.0 mm2) were obtained. Half of the specimens underwent microtensile bond strength testing, and the other half were subjected to the same tests after six months of storage. Failure mode was determined using an optical microscope (40×). The data were analyzed by a two-way analysis of variance followed by the Games-Howell test and Student t-test (preset alpha of 0.05). After seven days, SBU-RXU presented the highest mean bond strength, statistically different from only SBU-ARC (p<0.05). Most of the groups exhibited a statistically significant reduction in bond strength after 6 months (p<0.05), except SBP-RXU and SBU-ARC (p>0.05). The adhesive strategy, with different associations between adhesive systems and resin cements, as well as the use of a DCA, affected the bond strength of both amine-free and amine-based resin cements to a CAD/CAM composite.

Original and Repair Bulk Fracture Resistance of Particle Filler and Short Fiber-Reinforced Composites.

This study aimed to evaluate the original (OR) and repair (RR) fracture resistance of a semi-interpenetrating polymer network (semi-IPN)-based short fiber-reinforced composite compared to dimethacrylate-based composite materials by means of the V-notch test. Circular specimens (5×2 mm) with a centrally machined 90° V-shaped notch were prepared. Four bulk fill (Filtek Bulk Fill, Venus Bulk Fill, TetricEvo Ceram Bulk Fill, SDR), three microfilled hybrid (GC-Anterior, GC-Posterior, Z250), one nanofilled (SupremeXTE), and two short fiber-reinforced (Alert, everX Posterior) composites were selected. EverX Posterior was the semi-IPN material. Specimens (n=12/group) were either dry or water stored for 7 and 30 days, respectively, at 37°C and then loaded in two-point load until fracture. One-half of each tested specimen was used for the repair procedure. Repairing surfaces were diamond-bur ground, etched, and treated with silane containing universal adhesive (Scotchbond Universal) before repair. Three-way analysis of variance revealed a significant statistical difference between the groups ( p<0.05). The fracture resistance of dry-stored groups was greater than that of water-stored groups. The highest OR was observed for dry-stored Alert (23.4 N/mm), which significantly deteriorated in water (17.4 N/mm) ( p<0.05). The highest RR was observed for everX Posterior (20.0 N/mm), which did not deteriorate in water significantly (19.0 N/mm) ( p>0.05). The everX Posterior preserved the specimens' integrity at the final fracture load (ductile fracture), whereas all other materials fractured into two halves at the interface (adhesive failure). The only material that provided enhanced repair strength that was close to the original cohesive strength of the material was everX Posterior. The endurance of repaired restorations can be improved by using semi-IPN-based filling material.

Effect of Active Application on Bond Durability of Universal Adhesives.

The purpose of this study was to determine the effect of different adhesive application methods and etching modes on the dentin bond durability of universal adhesives under thermal cycling (TC). All-Bond Universal (Bisco), Adhese Universal (Ivoclar Vivadent), and Scotchbond Universal (3M ESPE) were used as adhesives. In total, 600 bovine teeth with exposed dentin were divided into 12 groups according to the type of adhesive and subjected to the following bonding procedures: 1) etch-and-rinse mode with active application; 2) etch-and-rinse mode with inactive application; 3) self-etch mode with active application; and 4) self-etch mode with inactive application. Bonded specimens were stored in distilled water at 37°C for 24 hours and then subjected to 5000, 10,000, 30,000, or 50,000 TC between 5°C and 55°C before shear bond strength (SBS) testing, creating a division into a total of five different storage conditions. Baseline specimens were stored in distilled water at 37°C for 24 hours. The SBS test was performed at a cross-head speed of 1.0 mm/min. Three-way analysis of variance revealed that all the factors of application mode, adhesive, and thermal cycle period significantly influenced the SBS values ( p<0.001), regardless of the etching mode. In the baseline groups, all of the tested adhesives with active application had higher SBS values than those with inactive application, regardless of etching mode. In the TC groups, significantly lower SBS values were observed at 50,000 TC with inactive application compared to those with active application, regardless of the etching mode. From the scanning electron microscopy observation of demineralized and deproteinized resin/dentin interfaces, dense resin tags longer than 50 μm were observed in the etch-and-rinse with active application group. On the other hand, the resin tags in self-etch mode were sparse, thin, and much shorter than those in etch-and-rinse mode. Comparing the penetration status of the resin tags with active and inactive application in self-etch mode, the resin tag penetration with inactive application was much lower than that with active application. Active application is effective in enhancing the dentin bond durability of universal adhesives. When using universal adhesives with different etching modes, practitioners should select the optimal etching mode and appropriate application method in accordance with the cavity conditions.

Effect of alumina-blasting pressure on adhesion of CAD/CAM resin block to dentin.

The aim of this study was to evaluate how alumina-blasting pressure affects the bond strength of CAD/CAM resin blocks (CRBs) to bovine dentin using two different types of resin cements. CRB slices were divided into three groups by alumina-blasting pressure, namely, untreated and 0.1 MPa and 0.2 MPa, and further divided into three subgroups by combination of CRBs surface treatment and types of cement: Scotchbond Universal and RelyX ultimate (RXB), Scotchbond Universal and RelyX unicem2 (U2B), ceramic primer and RelyX unicem2 (U2C). The CRB slices were then cemented to bovine dentin, microtensile bond strength test was performed and evaluated. Regardless of the alumina-blasting pressure, RXB group have the highest µTBS and bond strength tends to increase with increasing alumina-blasting pressure. Alumina-blasting to CRB surface by at an appropriate pressure and use of conventional resin cement were required to obtain strong adhesion with the tooth structure.

Effect of the demineralisation efficacy of MDP utilized on the bonding performance of MDP-based all-in-one adhesives

ObjectivesThe amounts of calcium salt of 10-methacryloyloxydecyl dihydrogen phosphate (MDP-Ca salt) and dicalcium phosphate dihydride (DCPD) with an amorphous phase produced by the demineralisation of enamel and dentin were determined using commercial MDP-based 2-hydroxyethyl methacrylate (HEMA)-containing and HEMA-free all-in-one adhesives. The effect of the amount of MDP-Ca salt produced on bonding performance to enamel and dentin was then characterized. MethodsThree types of commercial HEMA-containing adhesives (Scotchbond Universal Adhesive, Clearfil Tri-S Bond ND, Clearfil Tri-S Bond ND Quick), a commercial HEMA-free adhesive (G-Bond Plus) and an experimental HEMA-free adhesive were used. The reactant residues of each adhesive were prepared after interacting with enamel and dentin samples for 60 s. The amounts of MDP-Ca salt and amorphous DCPD produced were determined using a phosphorous-31 nuclear magnetic resonance technique. Enamel and dentin bond strengths were measured for each adhesive, with and without thermocycling. ResultsThe amounts of MDP-Ca salt and amorphous DCPD formed after interacting with enamel and dentin differed among the five adhesives and were independent of their pH values. Enamel showed a strong positive-correlation of the bond strength of the all-in-one adhesives to the amount of MDP-Ca salt produced, however, the dentin showed a weak negative-correlation. ConclusionThe HEMA-free all-in-one adhesives showed a greater efficacy to demineralise the enamel and dentin than the HEMA-containing all-in-one adhesives. The dentin showed a different effect of the amount of MDP-Ca salt produced on the bonding performance compared with enamel. Clinical significanceThe enamel bond strength of MDP-based all-in-one adhesives strongly contributes to the demineralisation efficacy by the incorporation of MDP, in contrast to the dentin bond strength. However, the efficacy of MDP-based all-in-one adhesives to demineralise the enamel and dentin is not directly related to the pH value of the MDP-based all-in-one adhesive.

Shear fatigue strength of resin composite bonded to dentin at physiological frequency.

The purpose of this study was to examine the shear fatigue strengths of a resin composite bonded to dentin. Three adhesive systems - a two-step self-etch adhesive (OptiBond XTR; Kerr) and two universal adhesives [Scotchbond Universal (3M ESPE) and G-Premio Bond (GC)] - were used in self-etch mode to bond a resin composite to dentin at a physiologic frequency of 2 Hz over 50,000, 100,000, and 1,000,000 cycles. A staircase method of fatigue testing was used. Twenty specimens were used for each test condition. There was no significant difference in shear fatigue strength across the cycling periods for the three individual adhesives. Differences in shear fatigue strength were found among the three adhesives within each cycling period. Regardless of the adhesive used in self-etch mode for bonding a resin composite to dentin, shear fatigue strength was not influenced by the number of cycles used for testing.