Mechanism of radiation-induced degradation in mechanical properties of polymer matrix composites

Four kinds of polymer matrix composites (filler, E-glass or carbon fibre cloth; matrix, epoxy or polyimide resin) and pure epoxy and polyimide resins were irradiated with 60Co γ-rays or 2 MeV electrons at room temperature. Mechanical tests were then carried out at 77 K and at room temperature. Following irradiation, the Young's (tensile) modulus of these composites and pure resins remains practically unchanged even at 170 MGy for both test temperatures. The ultimate strength, however, decreases appreciably with increasing dose. The dose dependence of the composite strength depends not only on the combination of fibre and matrix in the composite but also on the test temperature. A relationship is found between the composite ultimate strain and the matrix ultimate strain, thus indicating that the dose dependence of the composite strength is virtually determined by a change in the matrix ultimate strain due to irradiation. Based on this finding, we propose a mechanism of radiation-induced degradation of a polymer matrix composite in order to explain the dose dependence of the composite strength measured at 77 K and at room temperature.

Mechanical properties of polymer matrix composites at 77 K and at room temperature after irradiation with 60Co γ-rays

Ten different polymer matrix composites were irradiated with 60Co γ-rays at room temperature, and were examined with regard to the mechanical properties at 77 K and at room temperature. The radiation-induced degradation of these composites is observed much more significantly in the ultimate strength and in the shear modulus than in the Young's modulus. The radiation resistance of these composites depends primarily on the radiation resistance of matrix resins, which increases in the order diglycidyl ether of bisphenol A < tetraglycidyl| diaminodiphenyl methane < Kerimid 601. Comparison of the mechanical properties tested at 77 K and at room temperature demonstrates that the extent of radiation-induced decrease in the composite strength is appreciably greater in the 77 K test than in the room temperature test. Interpretation of these results is based on the competition between the two opposing effects due to the hardness and brittleness of matrix resins.