ProFile Ni-Ti Rotary Instruments Research Articles

A micro-computed tomographic evaluation of root canal filling with a single gutta-percha cone and calcium silicate sealer.

ObjectivesThe purpose of this study was to evaluate the void of root canal filling over time when a calcium silicate sealer was used in the single gutta-percha cone technique.Materials and MethodsTwenty-four J-shaped simulated root canals and twenty-four palatal root canals from extracted human maxillary molars were instrumented with ProFile Ni-Ti rotary instruments up to size 35/0.06 or size 40/0.06, respectively. Half of the canals were filled with Endoseal MTA and the other half were with AH Plus Jet using the single gutta-percha cone technique. Immediately after and 4 weeks after the root canal filling, the samples were scanned using micro-computed tomography at a resolution of 12.8 μm. The scanned images were reconstructed using the NRecon software and the void percentages were calculated using the CTan software, and statistically analyzed by 1-way analysis of variance, paired t-test and Tukey post hoc test.ResultsAfter 4 weeks, there were no significant changes in the void percentages at all levels in both material groups (p > 0.05), except at the apical level of the AH Plus Jet group (p < 0.05) in the simulated root canal showing more void percentage compared to other groups. Immediately after filling the extracted human root canals, the Endoseal MTA group showed significantly less void percentage compared to the AH Plus Jet group (p < 0.05).ConclusionsUnder the limitations of this study, the Endoseal MTA does not seem to reduce the voids over time.

Nano‐indentation testing of new and fractured nickel‐titanium endodontic instruments

To investigate the effect of cyclic fatigue on nickel-titanium (NiTi) endodontic instruments using a nano-indentation test. Eight ProFile NiTi rotary instruments (size 30, taper 0.06; Dentsply Maillefer, Ballaigues, Switzerland) were tested using a cyclic fatigue set-up until fracture. The fractured instruments and eight new NiTi instruments of the same size and taper were used for a nano-indentation test on the internal surfaces of a NiTi instruments in the region just adjacent to their fractured edge (group I) and in the same region of the new group (group II), and the cutting part beside the shaft for both instruments [group III (fractured) and group IV (new)]. Data were statistically analyzed using one-way analysis of variance and Games-Howell post hoc test. The alpha-type error was set at 0.05. Significant differences in terms of hardness and elastic modulus for each group (P < 0.05) were found, with group I having the lowest mean values followed by group III. Additionally, standard deviations increased remarkably after failure, as represented by groups I and III. The nano-indentation technique can be applied to determine the performance and the failure mechanism of NiTi instruments. The fatigue process revealed a significant decrease in the hardness and elastic modulus of the NiTi instrument. As indicated by the low hardness, the fatigue process did not result in work hardening but rather work softening.

Microleakage of resilon by methacrylate-based sealer and self-adhesive resin cement

The purpose of this study was to compare the apical microleakage in root canal filled with Resilon by methacrylate-based root canal sealer or 2 different self-adhesive resin cements. Seventy single-rooted extracted human teeth were sectioned at the CEJ perpendicular to the long axis of the roots with diamond disk. Canal preparation was performed with crown-down technique using Profile NiTi rotary instruments and GG drill. Each canal was prepared to ISO size 40, .04 taper and 1 mm short from the apex. The prepared roots were randomly divided into 4 experimental groups of 15 roots each and 5 roots each for positive and negative control group. The root canals were filled by lateral condensation as follows. Group 1: Guttapercha with AH-26, Group 2: Resilon with RealSeal primer & sealer, Group 3: Resilon with Rely-X Unicem, Group 4: Resilon with BisCem. After stored in , 100% humidity chamber for 7 days, the roots were coated with 2 layers of nail varnish except apical 3 mm. The roots were then immersed in 1% methylene blue dye for 7 days. Apical microleakage was measured by a maximum length of linear dye penetration after roots were separated longitudinally. One way ANOVA and Scheffe's post-hoc test were performed for statistical analysis. Group 1 showed the least apical leakage and there was no statistical significance between Group 2, 3, 4. According to the results, the self adhesive resin cement is possible to use as sealer instead of primer & sealant when root canal filled by Resilon.

Smear layer production of K3 and ProFile Ni-Ti rotary instruments in curved root canals: A comparative SEM study

The aim of this scanning electron microscopic study was to compare the quality and amounts of smear layer generated by 2 brands of nickel-titanium rotary instruments during canal preparation in the apical thirds of curved root canals. Forty mandibular mesial root canals with intact apex and mean curvature between 30 and 35 degrees were selected for this study. The root canals were randomly divided into 2 instrumentation groups of 15 each. Automated preparation was performed with ProFile (Dentsply Maillefer, Ballaigues, Switzerland; n = 15) and K3 (SybronEndo, Orange, Calif; n = 15) instrumentss using a crown-down technique. As a control group, barbed broaches (Mani; Matsutani Seisakusho, Takanezawa-Machi Tochibi-Ken, Japan; n = 10) were used to extirpate the necrotic pulp tissue from the root canals. All root canals were prepared to size #35. Glyde (File Prep, Dentsply Maillefer) was used as lubricant and 1% sodium hypochlorite solution as irrigant. At the conclusion of the experiments, all roots were split longitudinally and the root canal walls were examined at the apical third from 2 different perspectives using a scanning electron microscope. A 4-category scoring system for assessing the smear layer accumulation was used, and the resulting scores were statistically analyzed. Less smear layer was obtained in the K3 group at the selected apical third of curved root canals (P < .05). However, all instruments left a smear layer. The surface texture of the smear layer, in addition to the depth and the frequency of packed materials into the dentinal tubules, varied with instrument type. This finding may imply that, compared to ProFile, compression of the remaining smear layer is minimized when using the K3 rotary nickel-titanium system.

Analysis of Continuous-Wave Obturation Using a Single-cone and Hybrid Technique

This study analyzed the adaptation of gutta-percha to prepared root canal walls using two obturation techniques and determined the influence of the System-B plugger depth on filling adaptation. Fifty-six extracted human mandibular molars were instrumented using Profile NiTi rotary instruments, stratified based on curvature, then randomly distributed into two groups. Group 1 was obturated using the single-cone continuous-wave technique. Group 2 was obturated with a hybrid technique: lateral condensation followed by a continuous-wave down-pack. Based on System-B plugger penetration, teeth were divided into three subgroups: (a) < 3.5 mm, (b) 3.5 to 4.5 mm, and (c) > 4.5 mm. Roots were horizontally sectioned at 1 mm and 3 mm coronal to the apical foramen, stained, and photographed. Four evaluators scored the adaptation of gutta-percha to the prepared canal walls. In 100% (n = 56) of the samples, no statistically significant difference existed between the two obturation methods at 1-mm (x = 1.80, SD +/- 0.69) or 3-mm (x = 1.804, SD +/- 0.69) sections. Best results were obtained with a plugger depth 3.5 to 4.5 mm from the working length.

Surface analysis of ProFile instruments by scanning electron microscopy and X-ray energy-dispersive spectroscopy: a preliminary study.

The purpose of this preliminary study was to analyze surface irregularities on ProFile nickel-titanium (NiTi) rotary instruments before use, after sterilization by two different methods and after instrumentation of molar root canals. Five new ProFile NiTi rotary instruments with 0.04 taper, size 20, five instruments with 0.04 taper, size 25 and five with 0.06 taper, size 20 were analyzed by scanning electron microscopy (SEM) and X-ray energy-dispersive spectroscopy (EDS). The instruments were then divided into two groups: three of each taper and size were sterilized in a dry heat sterilizer, whilst two of each taper and size were sterilized in an autoclave. After inspection by the same techniques, the files were used to instrument six molar root canals, and again analyzed by SEM/EDS. Together with the usual machining defects, a variable amount of material containing mainly carbon and sulphur was found on the surface of new instruments. This material was not removed by standard cleaning and sterilization procedures. The use of the files for instrumentation of root canals eliminated a considerable amount of the adhered substance, but deposits rich in calcium and phosphorus accumulated on the remaining impurities. The adherence of dentine on surface deposits found on new ProFile instruments requires special cleaning, prior to sterilization.

Evaluation of Glyde File Prep in Combination with Sodium Hypochlorite as a Root Canal Irrigant

The purpose of this study using a scanning electron microscope was to investigate the efficacy of four different irrigation techniques after canal preparation with Profile Ni-Ti rotary instruments. A modified technique for the use of Glyde File Prep is proposed. Forty anterior teeth were divided into four groups, instrumented, and irrigated as follows: physiological solution (group A), 2.5% sodium hypochlorite (group B), 2.5% sodium hypochlorite and Glyde File Prep (group C), and 2.5% sodium hypochlorite and Glyde File Prep applied at the end of the preparation with sterile paper points (group D). After scanning electron microscopic evaluation at three different levels, debris, smear layer, and dentinal tubules were scored. Groups A and B had significantly more smear layer and less open tubules on the canal walls compared with the group C and group D samples. Differences in the mean amount of debris between group A samples and other irrigation regimes were statistically significant.

Cyclic fatigue of ProFile rotary instruments after clinical use.

The purpose of this study was to evaluate cyclic fatigue of .06 ProFile Ni-Ti rotary instruments after clinical use in molar teeth. In group 1, instruments size 40-15 were used in a crown-down technique using 2.5% NaOCl as an irrigant. Fifty-two molars were included and 13 sets of Profile Ni-Ti rotary instruments were used. Each set of instruments was used in four molars, and was steam autoclaved before each use. Group 2 (10 sets of new ProFile Ni-Ti rotary instruments) was the control group. Cyclic fatigue was tested by rotating the instruments in a 90 degrees metallic tube until they broke. One-way analysis of variance did not show any statistically significant differences amongst the files from both groups regarding cyclic fatigue. It was concluded that sterilization and clinical use in the presence of NaOCl did not lead to a decrease in the number of rotations to breakage of the files.

Analysis of forces developed during mechanical preparation of extracted teeth using Profile NiTi rotary instruments

The aim of this study was to analyse the vertical forces and torque developed in the root canal system of extracted teeth during mechanical preparation using ProFile NiTi instruments. Instrument wear and fracture is in great part due to the repeated application of forces and torque during the course of root-canal preparation but research into the direct relationship has been hampered by the lack of adequate measuring devices. Measurements of these forces and torque were made with a new force analyser device, the Endographe, that was equipped with a holder to record and generate graphs of the vertical forces and torque exerted during the preparations. These preparations was performed by endodontists or students either with a series of instruments of increasing size or with the crown-down pressureless technique. The mean values for the endodontists of the generated vertical forces and torque varied, respectively, from 4 to 6N and from 7.105 to 12.105 Nm for the step-back technique and from 2.9 to 4.2 N and from 18.105 to 20.105 Nm for the crown-down technique. This suggested that the crown-down technique generated lower stresses (lower torque and lower vertical forces), although these findings also depend on the shape of individual canals. The students initially showed wide variations in generated forces, with significantly lower vertical force the torque values. By the end of the experimental sessions their values were similar to those of the endodontists, which indicated improvement in the efficiency of manipulation. Further work is needed to investigate the relationship between the force and the torque data from this study and the incidence of instrument fracture with the two techniques, as the clinical implications are considerable. It must be noted, however, that the Endographe is unable to take into account the cutting efficiency of the instruments. The use of graphs provides a new approach to the analysis of mechanical preparation.

Analysis of forces developed during mechanical preparation of extracted teeth using Profile NiTi rotary instruments

Analysis of forces developed during mechanical preparation of extracted teeth using Profile NiTi rotary instruments