This paper presents a study of carbide precipitation, grain boundary segregation, and temper embrittlement in NiCrMoV rotor steels. One of the steels was high purity, one was doped with phosphorus, one was doped with tin, and one was commercial purity. In addition, two NiCrV steels, one high purity and one doped with phosphorus, were examined. Carbide precipitation was studied with analytical electron microscopy. It was found that after one hour of tempering at 600 ‡C only M3C carbides were precipitated in the NiCrMoV steels. These were very rich in iron. As the tempering time increased, the chromium content of the M3C carbides increased significantly, but their size did not change. Chromium rich M7C3 precipitates began to form after 20 hours of tempering, and after 50 hours of tempering Mo-rich M2C carbides were precipitated. Also, after 100 hours of tempering, the matrix formed bands rich in M3C or M7C3 and M2C particles. Tempering occurred more rapidly in the NiCrV steels. Grain boundary segregation was studied with Auger electron spectroscopy. It was found that the amount of phosphorus and tin segregation that occurred during a step-cooling heat treatment after tempering was less if a short time tempering treatment had been used. It will be proposed that this result occurs because the low temperature tempering treatments leave more carbon in the matrix. Carbon then compctes with phosphorus and tin for sites at grain boundaries. This compctition appears to affect phosphorus segregation more than tin segregation. In addition to these two impurity elements, molybdenum and nickel segregated during low temperature aging. The presence of molybdenum in the steel did not appear to affect phosphorus segregation. Finally, it will be shown that all of the steels that contain phosphorus and/or tin exhibit some degree of temper embrittlement when they are aged at 520 ‡C or are given a step-cooling heat treatment. Of the NiCrMoV steels, the phosphorus-doped steel showed the least embrittlement and the commercial purity steel the most. The phosphorus-doped NiCrV steel was also more susceptible to temper embrittlement than the phosphorus-doped NiCrMoV steel. This latter difference was attributed to molybdenum improving grain boundary cohesion. It was also found that as the segregation of phosphorus or tin to the grain boundaries increased, the measured embrittlement and the amount of intergranular fracture increased. However, there was a large amount of scatter in all of these data and the trends were only qualitative. All parts of this study are compared in detail to others in the literature, and general trends that can be discerned from all of these results are presented.