The demand for white-light luminescent materials for the white-light-emitting diodes (W-LEDs) field has been growing in modern life. In this work, a series of Sn2+ and Mn2+ ions co-doped highly transparent white-light emitting oxyfluoride glasses (precursor glass, PG) and Sr2LuF7 glass-ceramics (GC) were successfully prepared by the melt-quenching technique. Their luminescent and structural properties were investigated by the transmission spectra, excitation and emission spectra at different temperatures (300-500K), luminescent decay curves, XRD, and TEM characterizations. Upon excitation with ultraviolet (UV) light, tunable broadband blue-white light emissions of Sn2+ were obtained by adjusting the concentration of Sn2+ ions. A conspicuous energy transfer process from Sn2+ to Mn2+ was observed in Sn2+/Mn2+ co-doped samples. Tunable broadband luminescence between blue-white light and orange-red light regions and nearly pink-white light emission was realized by varying Mn2+ concertation. Furthermore, compared to PG samples, the emissions were enhanced in GC samples due to the crystallization of Sr2LuF7 nanocrystals. Excellent thermal stability was also performed in these Sn2+ doped PG and GC samples with a recovering value of 96% and 98.8%, respectively. Simultaneously, Sn2+ doped PG and GC samples also own good optical thermal sensitivities with an SA value of 2.28% and 2.47% K-1, respectively. Our results indicate that these Sn2+/Mn2+ co-doped PG and GC may serve as tunable light sources under UV excitation and have prospects on the ratiometric optical thermometry fields.