MoO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> prepared by oxidizing a Mo filament (oxidized MoO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ) with Al is a good replacement of a Au electrode for pentacene-based organic thin-film transistors (TFTs) (OTFTs). The oxidized MoO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /Al bilayer electrode shows better result than the laboratory-prepared pure MoO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /Al bilayer electrode. This process will save the cost of laboratory-prepared pure MoO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> . The OTFTs show a very good current on-off ratio of 1.6 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> and a field-effect mobility (μ) of 0.57 cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> /V·s. With this process, we can fabricate low-cost pentacene TFTs with better performance by using a very simple fabrication technique.