This article experimentally investigates the impact of silver (Ag) nano-particles inclusion and high pelletized pressure on the structural, morphological, and electrical properties of Cu0.5Tl0.5Ba2Ca2Cu3O10−δ (noted CuTl-1223) bulk system. The nano-(Ag) x /CuTl-1223 composites were synthesized using a two-step solid-state reaction process with added amount of Ag nano-particles ranging from 0 to 2.0 wt% of the total mass. These nano-composites were produced at both low and high pelletize pressure of 0.202 GPa. All prepared samples were characterized using valuable techniques such as X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS), Fourier Transform Infrared Spectroscopy (FTIR), and dc-resistivity measurement at low as well as high pelletized pressure, respectively. The structural investigation via the XRD technique indicated that Ag NPs did not affect the CuTl-1223 tetragonal structure, confirmed that Ag nano-particles were settled across the grain boundaries. SEM examination revealed a fine distribution of nano-sized silver (Ag) NPs among the CuTl-1223 grains, as well as improved weak-links and density of void/pores. The position of distinct vibrational oxygen modes in FTIR spectra showed no substantial alteration, indicating that the structural nature of the host CuTl-1223 phase was preserved. The electrical properties were studied using the four-point probe technique, and the activation energy were determined using Arrhenius law. The results of measurements showed that pelletization pressure of 0.202 GPa have an impact on the critical temperature of (Ag) x /CuTl-1223 composites. The superconducting critical temperature was enhanced from 99 K to 107 K at high-pressure of pelletization (0.202 GPa) as compared to low pressure, with = 0 ∼ 2.0 wt nano-particles addition to the host CuTl-1223 phase.