Abstract
Sodium alanate powder comprised of NaH and Al was doped with 3 mol% titanium chloride (TiCl3) and pelletized into highly compacted cylindrical pellets. The pelletization process was performed to improve thermal conductivity and volumetric hydrogen capacity of the metal hydride, compared to loose or tapped powder, which are vital requirements for on-board hydrogen storage applications. The pelletization process was performed over a range of 69–345 MPa (10–50 kPSI) with a 95% increase in density and improvement in thermal conductivity 18 times greater compared to powder at the maximum pelletization pressure (1.60 g/cm3 and 0.82 g/cm3; 9.09 W/m K and 0.50 W/m K, respectively). Hydrogen cycling capacities and kinetics were not adversely affected by the pelletization process although 10 cycles are required to obtain full hydrogen capacity. Pellet cycling capacity maintained a stable 4 wt% H2 over 50 cycles. Ti-doped NaH + Al pellets exhibited similar thermal cycling expansion as with the loose powder; within 30 cycles there was a 50% loss in pellet density and by 50 cycles the loss in pellet structural integrity made handling problematic.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have