Effect of multidirectional forging on microstructures and tensile properties of a particulate reinforced magnesium matrix composite

Abstract A particulate reinforced magnesium matrix composite prepared with stir casting was subjected to multidirectional forging (MDF). The results showed that after 1 MDF pass the grain size of matrix in the composites decreased compared with as-cast composite, and increased with increasing the MDF temperature from 370 °C to 450 °C. With increasing the MDF passes at 370 °C, the particle distribution of the composite was improved until 3 MDF passes while the grain size of matrix in the composite reached a minimum after 4 MDF passes. Both the yield strength and the ultimate tensile strength of the composite were enhanced with increasing the MDF passes.

Multidirectional forging of magnesium matrix composites: Effect on microstructures and tensile properties

A particulate reinforced magnesium matrix composite fabricated by stir casting was subjected to multidirectional forging (MDF) at a temperature of 420 °C. The results showed that grains of matrix in the composite were significantly refined after 1 MDF pass, and gradually refined till 3 MDF passes. The evolution of particle distribution in the composite during MDF was investigated by a window technique. It was shown that MDF led to an increase of the uniformity of the particle distribution. With increasing the MDF passes, both the tensile strength and the elongation to failure of the composite are significantly enhanced till 3 MDF passes.