Polycrystalline potassium chloride crystals alloyed with either RbCl, KBr, or EuCl2 have been irradiated with 1 MeV electrons at a dose rate of approximately 3.3 × 105 R/s. Measurements of the 10.6 μm absorption coefficient after each exposure indicated that the radiation induced infrared absorption saturated rapidly as a function of increasing electron exposure time. Measurements of the visible and near-infrared absorption spectra indicated no positive correlation between F-absorption centers and increased infrared absorption at 10.6 μm. A definite correlation was found between the density of F-aggregate centers and the change in 10.6 μm absorption. In particular, it is found that the largest changes in 10.6 μm absorption can be associated with the presence of R-centers in the mixed crystals. Polykristalline Kaliumchloridkristalle wurden mit Beigaben von RbCl, KBr oder EuCl2 hergestellt und mit 1 MeV-Elektronen bestrahlt. Die Dosis betrug annähernd 3,3 × 105 R/s. Messungen des Absorptionskoeffizienten bei 10,6 μm nach jeder Bestrahlung zeigen, daß die durch die Strahlung hervorgerufene Infrarotabsorption sich mit zunehmender Elektronenbestrahlungsdauer sehr schnell einem Sättigungswert nähert. Messungen im sichtbaren und im nahen IR-Spektralbereich zeigen keine positive Korrelation zwischen F-Absorptionszentren und steigender Infrarotabsorption bei 10,6 μm. Ein ausdrücklicher Zusammenhang wird zwischen der Dichte der F-Aggregatzentren und der Veränderung der Absorption bei 10,6 μm gefunden. Insbesondere stellt sich heraus, daß die größten Veränderungen der Absorption bei 10,6 μm mit der Anwesenheit von R-Zentren in den Mischkristallen in Zusammenhang gebracht werden können.