Abstract The influence of metal inert-gas arc welding (MIG) on the corrosion behavior of 6061-T6 aluminum alloy in a simulated tropical marine atmospheric environment (related to high temperature, high humidity and high salt spray) were examined by dry-wet alternate immersion corrosion tests. The equivalent conversion was used to design the accelerated test time. The results show that in the initial stage, the intermetallic compound, rich in Fe, Si and Cu, had little influence on corrosion resistance in the heat-affected zone. For a corrosion time of 3 days in a tropical marine atmospheric environment, the corrosion rate of the welded joint increased rapidly, even reaching 3.5 times that of the base metal. Though the corrosion products had significant impact on slowing down the corrosion rate, as with the base metal, the corrosion rate of the welded joint was nearly double that of the base metal during the longest cycle period involving alternate immersion corrosion tests for 20 days.