Medical Imaging Sensors Research Articles

Eu-doped CsBr phosphor as a new optically-stimulable phosphor material for medical x-ray imaging sensor

CsBr phosphor ceramics doped with different luminescence centres such as In2O3, Eu2O3, EuCl3, SmCl3, TbCl3, GdCl3 or NdCl3 as the candidate for a new optically-stimulable phosphor for medical X-ray imaging sensor were prepared using a conventional ceramic fabrication process. It was found that X-ray-irradiated Eu-doped CsBr (CsBr:Eu) exhibited intense optically stimulated luminescence (OSL). The peak wavelength of the OSL emission and stimulation spectra of CsBr:Eu phosphor ceramic sample were 450 and 690 nm, respectively. The dependence of OSL properties on the conditions of preparation of phosphor ceramic samples, such as Eu concentration, sintering temperature and sintering time, were studied. The optimum preparation conditions were also studied. It was found that the OSL intensity of CsBr:Eu phosphor ceramics fabricated under optimum preparation conditions is higher than that of commercially available imaging plates using BaFBr:Eu.

CsBr:Eu Phosphor Ceramics as a New Photostimulable Phosphor Material for Two Dimensional X-ray Imaging Sensor

CsBr phosphor ceramics doped with different luminescence center such as In203,EU203,EuC13, SmC13, TbC13 ,GdC13 or NdC13 as a candidate of a new photosimulable phosphor for medical x-ray imaging sensor are prepared using a conventional ceramic fabrication process. It is found that x-ray-irradiated Eu-doped CsBr (CsBr:Eu) exhibits intense photostimulated luminescence (P SL). The peak wavelength of the PSL emission and stimulation spectra of CsBr:Eu phosphor ceramic sample is 450 nm and 690 nm, respectively. The dependence of PSL properties on preparing conditions of phosphor ceramic samples,such as Eu concentration,sintering temperature and sintering time,is studied and the optimum preparing condition is also studied. It is found that the PSL intensity of CsBr:Eu phosphor ceramics fabricated under optimum preparation condition is higher than that of commercially available imaging plate usingBafBr:Eu.