Solubility of oxygen in liquid iron was measured by levitating liquid iron in contact with liquid iron oxide at known temperatures and removing samples of oxide and metal at equilibrium for analysis. Because of the protective layer of iron vapour which surrounds the metal, no special precautions are required to control the oxygen potential of the gas phase. Equilibrium between oxide and metal is attained in approximately 300 seconds. Solubilities at 1785, 1880 and 1960°C are, respectively, 0.45, 0.62 and 0.83 (± 0.02)% by weight. The results, together with earlier data of Taylor and Chipman, are represented by the equationlog 10 (wt % 0) = −6380/T(°k)+2.765in the range 1800–2230°K. The technique provides a new and useful method for the study of slag-metal equilibria. Résumé La solubilité de l'oxygene dans la fer liquide a été mesurée en faisant leviter du fer liquide en contact avec l°oxyde de fer liquide á température connue et en échantillonnant á ldeg;équilibre, pour fins d'analyse, de l'oxyde et du métal. Comme le fer est protége par sa vapeur, aucune précaution spéciale n'est nécessaire pour contrÔler le potentiel de l'oxygene de la phase gazeuse. L'équilibre entre Ie metal et l'oxyde est atteint en environ 400 secondes. A 1785, 1880 et 1960°C les solubilites sont respectivement de 0.45, 0.62 et 0.83 (± 0.02) % poids. Nos résultats, ainsi que les données de Taylor et Chipman, sont représentés par l'équation:log 10 (%poids 0) = −6380/T(°k)+2.765pour un intervalle de température s'etendant de 1800 a 2230°K. Cette technique procure une nouvelle methode poér l' étude des équilibres laitier-métal.