Layered Covalent Organic Frameworks Research Articles

Low‐Overpotential Electrocatalytic Water Splitting with Noble‐Metal‐Free Nanoparticles Supported in a sp3 N‐Rich Flexible COF

Covalent organic frameworks (COFs) are crystalline organic polymers with tunable structures. Here, a COF is prepared using building units with highly flexible tetrahedral sp3 nitrogens. This flexibility gives rise to structural changes which generate mesopores capable of confining very small (<2 nm sized) non‐noble‐metal‐based nanoparticles (NPs). This nanocomposite shows exceptional activity toward the oxygen‐evolution reaction from alkaline water with an overpotential of 258 mV at a current density of 10 mA cm−2. The overpotential observed in the COF‐nanoparticle system is the best in class, and is close to the current record of ≈200 mV for any noble‐metal‐free electrocatalytic water splitting system—the Fe–Co–Ni metal‐oxide‐film system. Also, it possesses outstanding kinetics (Tafel slope of 38.9 mV dec−1) for the reaction. The COF is able to stabilize such small‐sized NP in the absence of any capping agent because of the COF–Ni(OH)2 interactions arising from the N‐rich backbone of the COF. Density‐functional‐theory modeling of the interaction between the hexagonal Ni(OH)2 nanosheets and the COF shows that in the most favorable configuration the Ni(OH)2 nanosheets are sandwiched between the sp3 nitrogens of the adjacent COF layers and this can be crucial to maximizing their synergistic interactions.

Mechanochemical Synthesis of Chemically Stable Isoreticular Covalent Organic Frameworks

Three thermally and chemically stable isoreticular covalent organic frameworks (COFs) were synthesized via room-temperature solvent-free mechanochemical grinding. These COFs were successfully compared with their solvothermally synthesized counterparts in all aspects. These solvent-free mechanochemically synthesized COFs have moderate crystallinity with remarkable stability in boiling water, acid (9 N HCl), and base [TpBD (MC) in 3 N NaOH and TpPa-2 (MC) in 9 N NaOH]. Exfoliation of COF layers was simultaneously observed with COF formation during mechanochemical synthesis. The structures thus obtained seemed to have a graphene-like layered morphology (exfoliated layers), unlike the parent COFs synthesized solvothermally.

Tuning delamination of layered covalent organic frameworks through structural design

Exfoliation of a family of polyacetylenic porous layered covalent organic frameworks by means of a simple sonication procedure results in the obtention of nanolayer structures as observed by AFM and TEM measurements. Systematic AFM analysis of the isolated nanostructures reveals that the degree of exfoliation depends on the polymer architecture, thinner layers being observed when the pore size decreases.

A 2D Covalent Organic Framework with 4.7-nm Pores and Insight into Its Interlayer Stacking

Two-dimensional layered covalent organic frameworks (2D COFs) organize π-electron systems into ordered structures ideal for exciton and charge transport and exhibit permanent porosity available for subsequent functionalization. A 2D COF with the largest pores reported to date was synthesized by condensing 2,3,6,7,10,11-hexahydroxytriphenylene (HHTP) and 4,4'-diphenylbutadiynebis(boronic acid) (DPB). The COF was prepared as both a high surface area microcrystalline powder as well as a vertically oriented thin film on a transparent single-layer graphene/fused silica substrate. Complementary molecular dynamics and density functional theory calculations provide insight into the interlayer spacing of the COF and suggest that adjacent layers are horizontally offset by 1.7-1.8 Å, in contrast to the eclipsed AA stacking typically proposed for these materials.

On the reticular construction concept of covalent organic frameworks

The concept of reticular chemistry is investigated to explore the applicability of the formation of Covalent Organic Frameworks (COFs) from their defined individual building blocks. Thus, we have designed, optimized and investigated a set of reported and hypothetical 2D COFs using Density Functional Theory (DFT) and the related Density Functional based tight-binding (DFTB) method. Linear, trigonal and hexagonal building blocks have been selected for designing hexagonal COF layers. High-symmetry AA and AB stackings are considered, as well as low-symmetry serrated and inclined stackings of the layers. The latter ones are only slightly modified compared to the high-symmetry forms, but show higher energetic stability. Experimental XRD patterns found in literature also support stackings with highest formation energies. All stacking forms vary in their interlayer separations and band gaps; however, their electronic densities of states (DOS) are similar and not significantly different from that of a monolayer. The band gaps are found to be in the range of 1.7–4.0 eV. COFs built of building blocks with a greater number of aromatic rings have smaller band gaps.