AbstractWhen composite honeycomb sandwich structures are subjected to low energy impacts, the upper panel or the honeycomb core often suffers large damages, which are invisible, but affects the structural safety. To achieve non‐destructive detection of these damages, an epoxy resin film (ERF) was designed as a functional coating to display the internal failure features on structure surface. The effect of low energy impacts on the damage modes of the ERF was first investigated, and then the correspondence between the ERF damage characteristics and the structural internal failure was established. Simulation and experimental results showed that with the increase of impact energy, cracks on the ERF expanded from the radial radiation with a small extension range to the circumferential pattern with an increased damage area. Meanwhile, localized delamination appeared inside the upper panel, while the degree of flexure and crushing damage to the core continued to increase. Based on the analysis of the crack extension pattern of the ERF and the damage state of the upper panel and honeycomb core, a specific link between the ERF crack characteristics and the internal damages to the sandwich structure was obtained, which might offer a novel non‐destructive testing method for composite impact damages.Highlights Low energy impact damage in honeycomb sandwich structures was a concern. Impact damage response of epoxy resin film on sandwich composites was studied. Crack extension of the film showed a particular change from radial to annular. Specific link between film crack and sandwich structure damage was established. The results would be helpful for damage detection in sandwich composites.