Chemically densified coating formed on the surface of austenitic stainless steel (SUS 316) was examined for compatibility with molten lithium-lead eutectic alloy (Li17Pb83) and tritium permeability. The chemically densified coating (CDC) consisting of SiO 2 particles and a Cr 2O 3 matrix with a thickness of 60 μm was unstable in contact with the molten alloy as predicted from a thermodynamic calculation at 600°C, and it was degraded in several days. In an in-pile experiment, specimens with the coating on the front surface or the rear surface were immersed in Li17Pb83 molten alloy, and their tritium permeabilities were measured. The permeability of the former was reduced to 1 10 of the ideal value in the diffusion-limited case, while that of the latter was less than 1 100 of the diffusion-limited value even in a pure H 2 atmosphere. It is concluded that CDC is quite effective to reduce tritium permeability in the condition of not contacting molten Li17Pb83 alloy.