Copper nanoparticles (NPs) with an average particle diameter of 50–60 nm were successfully obtained by reducing an aqueous solution of a copper(II)-nitrilotriacetic acid complex with an aqueous hydrazine solution at room temperature under an air atmosphere. Copper NP-based nanopastes were printed onto a glass substrate using a metal screen mask and pressureless sintered under a nitrogen atmosphere at 200 °C for 30 min. The electrical resistivity of the resulting copper electrode was 16 μΩ · cm. For a metal-to-metal bonding test, copper nanopaste was printed on an oxygen-free copper plate, another oxygen-free copper plate was placed on top, and the bonding strength between the copper plates when pressureless sintered under a nitrogen atmosphere at 200 °C for 30 min was 39 MPa. TEM observations confirmed that highly crystalline metal bonding occurred between the copper NPs and the copper plate to introduce the ultrahigh strength. The developed copper NPs could provide promising advances as nanopastes for sustainable fabrication of copper electrodes and die attachment materials for the production of next-generation power semiconductors.