Hollow Latex Particles Research Articles

Drying and collapse of hollow latex

Hollow latex particles are used as white pigments for paints and paper coatings. In the coating dispersion, each hollow particle is filled with water. As the coating dries, water vacates the latex, leaving an air-filled void sized to scatter light (~0.5 μm) within each particle. Examinations of dried coatings reveal that hollow particles can collapse, decreasing their light scattering efficiency. Cryogenic scanning electron microscopy (cryoSEM) was used to characterize the microstructure of coatings containing hollow latex during drying. Images suggest latex voids empty after air invades into the coating interstitial space and collapse occurs late in the drying process. The effects of temperature (10–60°C), humidity (20–80%), and binder concentration (0–30 wt%) on particle collapse were also studied through SEM of dried coating surfaces. High drying temperature, high humidity, and low binder concentrations promoted collapse. For hollow latex particles with porous shell walls, temperature and humidity had little effect, whereas binder increased collapse. From these results, a theoretical model is proposed. During drying, diffusion of water from the particle creates a vacuum inside the latex. The vacuum is either relieved by nucleation of a gas bubble from the dissolved air in the water-filled particle or it causes the particle to collapse by buckling.

Preparation and structure control of hollow polymer particles: Influence of seeded emulsion polymerization and alkalization treatment process

AbstractHollow polymer latex particles containing a hydrophilic core were prepared by seeded emulsion polymerization with MAA/BA/MMA/St as comonomers, followed by stepwise alkalization treatment with ammonia. The size and morphology of composite latex particles was determined by TEM. The effects of the seeded emulsion polymerization conditions and alkalization treatment on the size and hollow structure of latex were investigated. The results showed that the optimum content of crosslinking agent in the shell polymers was about 0.5–1.0 wt %, emulsifier was about 0.8–1.1 wt %, and the core/shell weight ratio was 1/7. To obtain uniform hollow latex particles with large size, the starved feeding technique should be adopted in seeded emulsion polymerization, and the neutralization temperature should equal to the Tg of the shell polymer. Then, the obtained polymer particles under this condition had an excellent hollow structure. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009

Facile preparation and characterization of hollow poly(St-co-MMA-co-BA-co-MAA) core–double shell latex nanoparticles for electrophoretic displays

Novel core–double shell particles with poly(methyl methacrylate-co-butyl acrylate) (PMMA-co-BA) as the cores, poly(methyl methacrylate-co-butyl acrylate-co-methacrylic acid) (PMMA-co-BA-co-MAA) as the inner shells, poly(styrene-co-methyl methacrylate) (PS-co-MMA) as the outer shells were prepared by soap-free emulsion polymerization. The acid–alkali osmotic swelling processes were made before the outer shells wrapped for bigger aperture. The optimal experiment conditions were summarized. The morphology and size of the hollow latex particles were observed by transmission electron microscopy. The results showed that the uniform sizes of the hollow latex particles were about 230nm. The electrophoretic mobility of them in tetrachloroethylene was 0.91×10−10m2V−1s−1, and the Zeta-potential was 5.87mV. The results showed that the hollow polymer particles can used as background particles.

Cross-sectional analysis of hollow latex particles by focused ion beam–scanning electron microscopy

Cross-sectional analysis of hollow latex particles by focused ion beam–scanning electron microscopy

Preparation of monodispersed hollow polymer particles by seeded emulsion polymerization under low emulsifier conditions

AbstractIn a low emulsifier system, the MMA‐BA‐MAA copolymer emulsions were prepared as seed latices and the seeded emulsion polymerization of MMA‐MAA‐DVB was consequently carried out to prepare carboxylated core particles. The hydrophobic shell was then synthesized onto the core using styrene, acrylonitrile, and divinylbenzene as comonomers. The hollow latex particles were obtained by alkalization treatment of the core‐shell latex particles. The effects of the feeding rate of monomer mixture, contents of emulsifier SDBS and crosslinking agent DVB, and ratio of the monomers during the core stage and shell stage on the morphology and volume expansion of the latex particles were investigated. The results show that the monodispersed hollow latex particles with large size can be obtained when the feeding rate is 0.1 g/min, SDBS content is 0.15 and 0.2 wt % during the core stage and shell stage, respectively, DVB contents are 1% during the preparation of shell copolymers, and the monomer ratio of the core particle to shell layer is 1 : 8. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 1505–1510, 2005

Hollow latex particles as submicrometer reactors for polymerization in confined geometries

AbstractA method was developed for free‐radical polymerization in the confines of a hollow latex particle. Hollow particles were prepared via the dynamic swelling method from polystyrene seed and divinylbenzene and had hollows of 500–1000 nm. So that these hollow poly(divinylbenzene) particles could function as submicrometer reactors, the particles were filled with a monomer (N‐isopropylacrylamide) via the dispersion of the dried particles in the molten monomer. The monomer that was not contained in the hollows was removed by washing and gentle abrasion. Free‐radical polymerization was then initiated by γ radiolysis in the solid state. Transmission electron microscopy showed that poly(N‐isopropylacrylamide) formed in the hollow interior of the particles, which functioned as submicrometer reactors. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5706–5713, 2004