AbstractAmong the magnetic metal/semiconductor contacts, the Fe/GaAs system has been widely studied owing to its potential applications in electronic devices. In contrast, there are not many studies concerning the Fe/AlxGa1−xAs contact, and in particular there are no reports concerning the changes induced in the interfacial zone by the presence of Al. In this work, thin polycrystalline iron films were deposited by ion beam sputtering at room temperature on a 300 nm thick Al0.25Ga0.75As layer grown by molecular beam epitaxy onto GaAs(001). X‐ray diffraction analysis showed that the iron films are polycrystalline, and indications of a (002) texture of the film were observed. The fine scale analysis of the interface was achieved by high‐resolution transmission electron microscopy (HRTEM) observations, the results of which are compared with the physicochemical information obtained from electron‐induced x‐ray emission spectroscopy, by analysing the Al 3p valence states at the Fe/AlxGa1−xAs interface. The HRTEM experiments on cross‐section samples indicate that the interfacial zone between iron and AlGaAs is limited to <1.5 nm in thickness. X‐ray emission spectroscopy showed the presence of Al atoms in an FeAl‐like environment at the interface, and the existence of wrong bonds and point defects. The estimated width of the perturbed interface (2.0 ± 0.5 nm) is in agreement with the HRTEM results. Copyright © 2003 John Wiley & Sons, Ltd.