Starting from thermoanalytic measurements of amorphous material with a composition of 40 BaO – 33 B2O3 – 27 Fe2O3 (mole - %) the onset temperatures of four exothermic reaction peaks have been obtained. On the basis of this results the amorphous material was tempered under different conditions (heating rate and tempering time). The resulting reaction products were analyzed by X – ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), chemical analyses and by a vibrating sample magnetometer (VSM) to obtain information about their chemical composition, their structure and their magnetic properties. In contrast to former studies [2,3,4] it was found, that first an iron – rich phase forms at temperatures about 520 °C – 560 °C [5] followed by the crystallization of BaB2O4. Neue Ergebnisse zum Kristallisationsverhalten von Bariumhexaferrit in einer Glasmatrix Ausgehend von thermonalytischen Messungen an amorphem Material der Zusammensetzung 40 BaO – 33 B2O3 – 27 Fe2O3 (Mol - %) wurden die Onsettemperaturen von vier exothermen Reaktionspeaks ermittelt. Unter Nutzung dieser Ergebnisse wurde das amorphe Material unter verschiedenen Bedingungen (Heizrate, Temperzeit) getempert. Die entstandenen Reaktionsprodukte wurden mittels Röntgenbeugung (XRD), Rasterelektronenmikroskopie (REM), Transmissionselektronenmikroskopie (TEM), chemischen Analysen und Vibrationsmagnetometer (VSM) hinsichtlich ihrer Struktur und ihrer magnetischen Eigenschaften untersucht. Im Gegensatz zu früheren Untersuchungen [2,3,4] wurde herausgefunden, dass zuerst die Ausbildung einer eisenreichen Phase im Temperaturbereich von 520 °C – 560 °C stattfindet [5], worauf sich die Kristallisation von BaB2O4 anschließt.