Single crystals of the oxidephosphates Ti IIITi IV 3O 3(PO 4) 3 (black), Cr III 4Ti IV 27O 24(PO 4) 24 (red-brown, transparent), and Fe III 4Ti IV 27O 24(PO 4) 24 (brown) with edge-lengths up to 0.3 mm were grown by chemical vapour transport. The crystal structures of these orthorhombic members (space group F2 dd ) of the lazulite/lipscombite structure family were refined from single-crystal data [Ti IIITi IV 3O 3(PO 4) 3: Z=24, a=7.3261(9) Å, b=22.166(5) Å, c=39.239(8) Å, R 1=0.029, w R 2=0.084, 6055 independent reflections, 301 variables; Cr III 4Ti IV 27O 24(PO 4) 24: Z=1, a=7.419(3) Å, b=21.640(5) Å, c=13.057(4) Å, R 1=0.037, w R 2=0.097, 1524 independent reflections, 111 variables; Fe III 4Ti IV 27O 24(PO 4) 24: Z=1, a=7.4001(9) Å, b=21.7503(2) Å, c=12.775(3) Å, R 1=0.049, w R 2=0.140, 1240 independent reflections, 112 variables). For Ti IIITi IVO 3(PO 4) 3 a well-ordered structure built from dimers [Ti III,IV 2O 9] and [Ti IV,IV 2O 9] and phosphate tetrahedra is found. The metal sites in the crystal structures of Cr 4Ti 27O 24(PO 4) 24 and Fe 4Ti 27O 24(PO 4) 24, consisting of dimers [ M IIITi IVO 9] and [Ti IV,IV 2O 9], monomeric [Ti IVO 6] octahedra, and phosphate tetrahedra, are heavily disordered. Site disorder, leading to partial occupancy of all octahedral voids of the parent lipscombite/lazulite structure, as well as splitting of the metal positions is observed. According to Guinier photographs Ti III 4Ti IV 27O 24(PO 4) 24 ( a=7.418(2) Å, b=21.933(6) Å, c=12.948(7) Å) is isotypic to the oxidephosphates M III 4Ti IV 27O 24(PO 4) 24 ( M III: Cr, Fe). The UV/vis spectrum of Cr 4Ti 27O 24(PO 4) 24 reveals a rather small ligand-field splitting Δ o=14,370 cm −1 and a very low nephelauxetic ratio β=0.72 for the chromophores [Cr IIIO 6] within the dimers [Cr IIITi IVO 9].