Abstract— Fatigue tests conducted under fully reversed cyclic torsion, with and without superimposed axial static tension/compression loads, were carried out using hour‐glass smooth specimens in laboratory air. A high strength spring steel and a 316L stainless steel, were employed to evaluate the effects of mean stress on fatigue performance. Experimental test results show that a biaxial tensile/compressive mean stress had no influence on the cyclic stress‐strain response in both materials. However a biaxial tensile mean stress was found to be detrimental to fatigue life of the high strength spring steel but had no effect on the total fatigue life of 316L stainless steel. A compressive mean stress was found to be beneficial to the life of both steels. The fatigue behaviour of the two materials was investigated by experimental observations and the application of theoretical analyses of short crack growth behaviour. Based upon the analysis of surface acetate replicas it has been found that fatigue crack growth is material/stress‐state dependent. A biaxial tensile static stress promoted a change in the direction of the Stage I (mode II) crack from the longitudinal direction to a plane normal to the specimen axis in the high strength steel but not in the stainless steel. Consequently a different growth behaviour of Stage I (mode II) cracks was observed for the two materials. The effect of a biaxial mean stress on fatigue crack growth behaviour of the two materials is analysed and described in some detail.