Gold Bipyramids Research Articles

Growth of Gold Nanorods and Bipyramids Using CTEAB Surfactant

Gold nanorods and bipyramids have been synthesized using the seed-mediated approach in aqueous cetyltriethylammonium bromide (CTEAB) solutions in the presence of silver nitrate. Gold nanoparticle seeds that are stabilized with either CTEAB or sodium citrate have been used. The use of the CTEAB-stabilized seeds gives gold nanorods in high yield in one step with the longitudinal plasmon wavelength ranging from 750 to 1030 nm, depending on the amount of the seeds. The longitudinal plasmon wavelength can be extended to 1100 nm by the use of a two-step growth method. The growth of gold nanorods in CTEAB solutions takes 5-10 h, more than 5 times slower than that in cetyltrimethylammonium bromide solutions at the same concentration of surfactants. The use of the citrate-stabilized seeds gives both gold bipyramids and a small percentage of gold nanorods. The longitudinal plasmon wavelength of the bipyramids is tunable from 700 to 1100 nm by varying the amount of the citrate-stabilized seeds. The growth of gold bipyramids takes more than 1 day. Transmission electron microscopy characterizations reveal that the gold nanorods grown from both types of gold nanoparticle seeds are single-crystalline and that the gold bipyramids are penta-twinned.

Preparation and optical properties of silver chalcogenide coated gold nanorods

A homogeneous layer of silver sulfide or selenide was coated onto gold nanorods in aqueous solution by exposing Au/Ag core/shell nanorods to S2− or Se2− in an oxidizing environment. The formation of the silver chalcogenide layers was confirmed by transmission electron microscopy (TEM) and selective area electron diffraction (SAED). The longitudinal plasmon resonance of the gold nanorods shifted to the red and was attenuated. The experimental spectra agree well with a simulation based on confocal ellipsoids in the quasi-static limit. The synthetic procedure was also employed to coat silver sulfide or selenide onto gold bipyramids. A red-shift of the longitudinal plasmon resonance was also seen, although the coating was not as homogeneous. These novel composite materials may present interesting nonlinear optical properties.

Mechanism of Silver(I)-Assisted Growth of Gold Nanorods and Bipyramids

The seed-mediated growth of gold nanostructures is shown to be strongly dependent on the gold seed nanocrystal structure. The gold seed solutions can be prepared such that the seeds are either single crystalline or multiply twinned. With added silver(I) in the cetyltrimethylammonium bromide (CTAB) aqueous growth solutions, the two types of seeds yield either nanorods or elongated bipyramidal nanoparticles, in good yields. The gold nanorods are single crystalline, with a structure similar to those synthesized electrochemically (Yu, Y. Y. et al. J. Phys. Chem. B 1997, 101, 6661). In contrast, the gold bipyramids are pentatwinned. These bipyramids are strikingly monodisperse in shape. This leads to the sharpest ensemble longitudinal plasmon resonance reported so far for metal colloid solutions, with an inhomogeneous width as narrow as 0.13 eV for a resonance at approximately 1.5 eV. Ag(I) plays an essential role in the growth mechanism. Ag(I) slows down the growth of the gold nanostructures. Ag(I) also leads to high-energy side facets that are {110} for the single crystalline gold nanorods and unusually highly stepped {11n} (n approximately 7) for the bipyramid. To rationalize these observations, it is proposed that it is the underpotential deposition of Ag(I) that leads to the dominance of the facets with the more open surface structures. This forms the basis for the one-dimensional growth mechanism of single crystal nanorods, while it affects the shape of the nanostructures growing along a single twinning axis.