Magnetization, grain size, structure, and temperature-dependent dielectric permittivity of BiFeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> , (BiFeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> , <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.95</sub> (BaTiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ) <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.05</sub> -(BaTiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> )0.05(5%BTO-BFO), and (Bi <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.95</sub> Ba <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.05</sub> )(Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.95</sub> Ti <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.05</sub> )O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> [5%(Ba, Ti)-BFO] ceramics have been carried out. BFO and 5%BTO-BFO exhibit an typical antiferromagnetic behavior, whose magnetization curve is linear with magnetic field at room temperature. The magnetic hysteresis loop of 5%(Ba,Ti)-BFO ceramic shows a weak ferromagnetic behavior with a small remanent magnetization of about 0.01 emu/g possibly due to a higher density in the grain matrix. This result also implies that the A-and B-site substitutions with Ba <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2+</sup> and Ti <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4+</sup> could efficiently suppress the spiral magnetic modulation. The magnetic susceptibilities of BFO, 5%BTO-BFO, and 5%(Ba,Ti)-BFO ceramics are about 1.9 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-5</sup> , 5.43 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-6</sup> , and 8.67 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-6</sup> emu/gOe, respectively. Frequency-dependent dielectric maxima were observed in BFO, 5%BTO-BFO, and 5%(Ba,Ti)-BFO ceramics upon heating. This dielectric response is likely triggered by the antiferromagnetic-paramagnetic transition near the Neel temperature.