In this report, we have studied field-effect transistors (FETs) using low-density alumina for electrolytic gating. Device layers have been prepared starting from the structured ITO glasses by printing the In <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> channels, low-temperature atomic layer deposition (ALD) of alumina (Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ), and printing graphene top gates. The transistor performance could be deliberately changed by alternating the ambient humidity; furthermore, ID,ON/ID,OFF-ratios of up to seven orders of magnitude and threshold voltages between 0.66 and 0.43 V, decreasing with an increasing relative humidity between 40% and 90%, could be achieved. In contrast to the common usage of Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> as the dielectric in the FETs, our devices show electrolyte-typegating behavior. This is a result from the formation of protons on the Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> surfaces at higher humidities. Due to the very high local capacitances of the Helmholtz double layers at the channel surfaces, the operation voltage can be as low as 1 V. At low humidities (≤30%), the solid electrolyte dries out and the performance breaks down; however, it can fully reversibly be regained upon a humidity increase. Using ALD-derived alumina as solid electrolyte gating material, thus, allows low-voltage operation and provides a chemically stable gating material while maintaining low process temperatures. However, it has proven to be highly humidity-dependent in its performance.