The study demonstrated the successful fabrication of novel stainless steels by direct laser metal deposition with the aim of investigating the impact of niobium content (Nb = 0, 0.25, 0.75, 1.25 wt%) on their microstructure and electrochemical properties. The microstructure and phase evolution of the as-built stainless steels were studied using scanning electron microscope (SEM) and electron back-scatter diffraction (EBSD). Corrosion behavior of the samples was evaluated using electrochemical workstation in 3.5 wt% NaCl. Experimental results have shown that the crystal structure of as-built stainless steels was BCC with a small trace of dispersive carbides and FCC phase. Grain refinement was observed with increasing niobium content. Large-angle boundaries were obtained in different Nb-containing samples with distribution from 50° to 60°. An increase in niobium content extremely improved the corrosion resistance of as-built stainless steels and the as-built samples with 1.25 wt% exhibited the best corrosion resistance among the tested samples as indicated by its lowest corrosion rate, which was an order of magnitude lower than that of Nb-free samples.