The effects of Ce content and annealing temperature on the electromotive force produced by spin Seebeck devices fabricated using CexY3−xFe5O12 deposited by metal–organic decomposition was investigated. The Ce content was first varied () for a fixed annealing condition of 3 h at 900 °C. It was found that increasing the Ce content led to a decrease in electromotive force, which meant that x = 0 was the optimum Ce content. Next, the effect of annealing temperature was investigated for a Ce1Y2Fe5O12 film for an annealing time of 14 h. The highest electromotive force of 24.0 µV/50 °C was obtained for a sample annealed for 14 h at 800 °C, although the X-ray diffraction peaks were weaker than those for a sample annealed for 14 h at 950 °C.