A large peak in the thermally-stimulated depolarization current (TSDC) is observed for CeO2 ceramics doped with cations of lower valence. The peak is shown to be a Maxwell-Wagner effect due to the presence of a high resistivity layer about grain boundaries, the same mechanism that gives rise to the “grain boundary effect” in the ac conductivity. This peak may be utilized to obtain values of the lattice ionic conductivity at temperatures well below those at which ac measurements can conveniently be made. It is also shown how to eliminate this peak in order to be able to study the much smaller peaks due to reorientation of dipolar defects. Ein groses Maximum in dem thermisch stimulierten Depolarisationsstrom (TSDC) wird fur CeO2-Keramik, dotiert mit Kationen niedriger Valenz, beobachtet. Es wird gezeigt. das das Maximum ein Maxwell-Wagner Effekt ist, der von einer Hochwiderstandsschicht, welche die Korngrenzen umgibt, verursacht wird. Dieses ist derselbe Mechanismus der den „Korngrenzen-Effekt” in Wechselstromexperimenten ergibt. Dieses Maximum kann benutzt werden, um die ionische Gitter-leitfahigkeit zu erhalten bei Temperaturen viel niedriger als solche bei denen Wechselstromessungen leicht durchgefuhrt werden konnen. Es wird auch gezeigt, wie dieses Maximum eliminiert werden kann, um die kleineren Maxima, die durch Reorientierung von Dipolfehlern verursacht sind, zu studieren.