Directional melting of binary systems in the absence of convection is analyzed for concurrent compositional changes at the crystal-melt interface. It is shown that steady-state conditions cannot normally be reached during seeding and that the growth interface temperature during the ensuing initial stages of growth is a function of backmelt conditions. The theoretical treatment is numerically applied to Hg 1- x Cd x Te and Ga-doped Ge.