ObjectiveTo investigate the effectiveness of a d-enantiomeric antibiofilm peptide (DJK-5) on the anticorrosion ability of titanium (Ti) with different surface roughness against Streptococcus mutans biofilms. MethodsCommercially pure Ti disks with machined (MA, smooth) or sandblasted + acid-etched (SLA, rough) surfaces were prepared and characterized. All disks were divided into three groups: a positive control (PC) group with S. mutans, a DJK-5-treated group, and a negative control (NC) group without S. mutans. Biofilm formation and corrosion on Ti surfaces were determined by confocal laser scanning microscopy and scanning electron microscopy after 2 and 6 days, and the electrochemical properties were evaluated. ResultsTen μg/mL of DJK-5 killed 83.3 % and 87.4 % of biofilms on SLA and MA Ti surfaces, respectively after 2 days, and 72.9 % and 77.7 % after 6 days, with more bacteria surviving on SLA surfaces with higher roughness (p < 0.05). DJK-5 treatment induced less surface defects with tiny pit corrosion than PC. DJK-5 treatment when compared to PC, led to electrochemical properties more reflecting NC surfaces, including significantly less negative corrosion potential, lower corrosion current, and higher passive film resistance (p < 0.05). SLA surfaces exhibited higher current density and lower resistance than MA surfaces (p < 0.05). ConclusionDJK-5 effectively enhanced the corrosion resistance of Ti with different surface roughness while killing S. mutans biofilms, and smooth surfaces were more susceptible to peptide treatment. Clinical significanceThe antibiofilm peptide is promising for promoting the anticorrosion ability of Ti against biofilms, thereby preventing biofilm-related infections.